Fabrication and Characterization of Aligned Flexible Lead-Free Piezoelectric Nanofibers for Wearable Device Applications

Nanomaterials (Basel). 2018 Mar 29;8(4):206. doi: 10.3390/nano8040206.

Abstract

Flexible lead-free piezoelectric nanofibers, based on BNT-ST (0.78Bi0.5Na0.5TiO₃-0.22SrTiO₃) ceramic and poly(vinylidene fluoride-trifluoroethylene) (PVDF-TrFE) copolymers, were fabricated by an electrospinning method and the effects of the degree of alignment in the nanofibers on the piezoelectric characteristics were investigated. The microstructure of the lead-free piezoelectric nanofibers was observed by field emission scanning electron microscope (FE-SEM) and the orientation was analyzed by fast Fourier transform (FFT) images. X-ray diffraction (XRD) analysis confirmed that the phase was not changed by the electrospinning process and maintained a perovskite phase. Polarization-electric field (P-E) loops and piezoresponse force microscopy (PFM) were used to investigate the piezoelectric properties of the piezoelectric nanofibers, according to the degree of alignment-the well aligned piezoelectric nanofibers had higher piezoelectric properties. Furthermore, the output voltage of the aligned lead-free piezoelectric nanofibers was measured according to the vibration frequency and the bending motion and the aligned piezoelectric nanofibers with a collector rotation speed of 1500 rpm performed the best.

Keywords: aligned arrays; electrospinning; lead-free piezoelectric nanofiber; nanofiber composites; piezoelectric devices.