MOF-Derived Hierarchical MnO-Doped Fe3O4@C Composite Nanospheres with Enhanced Lithium Storage

ACS Appl Mater Interfaces. 2018 Apr 4;10(13):10974-10985. doi: 10.1021/acsami.8b01358. Epub 2018 Mar 26.

Abstract

Hierarchically nanostructured binary/multiple transition-metal oxides with electrically conductive coatings are very attractive for lithium-ion batteries owing to their excellent electrochemical properties induced by their unique compositions and microstructures. Herein, hierarchical MnO-doped Fe3O4@C composite nanospheres are prepared by a simple one-step annealing in Ar atmosphere, using Mn-doped Fe-based metal-organic frameworks (Mn-doped MIL-53(Fe)) as precursor. The MnO-doped Fe3O4@C composite particles have a uniform nanosphere structure with a diameter of ∼100 nm, and each nanosphere is composed of clustered primary nanoparticles with an amorphous carbon shell, forming a unique hierarchical nanoarchitecture. The as-prepared hierarchical MnO-doped Fe3O4@C composite nanospheres exhibit markedly enhanced lithium-storage performance, with a large capacity of 1297.5 mAh g-1 after 200 cycles at 200 mA g-1. The cycling performance is clarified through analyzing the galvanostatic discharge/charge voltage profiles and electrochemical impedance spectra at different cycles. The unique microstructures and Mn element doping of the hierarchical MnO-doped Fe3O4@C composite nanospheres lead to their enhanced lithium-storage performance.

Keywords: MnO-doped Fe3O4; anode; carbon coating; hierarchical structure; lithium-ion batteries; nanosphere.