WB2: not a superhard material for strong polarization character of interlayer W-B bonding.

Author information

1
State Key Laboratory of Superhard Materials, Jilin University, Changchun 130012, China. zhupw@jlu.edu.cn.

Abstract

In this work, the structure of WB2 synthesized at high pressure and high temperature (HPHT) was accurately determined by X-ray diffraction and Rietveld refinement. Its asymptotic Vickers hardness (Hv) value is 25.5 GPa which is much lower than the previous theoretical results (36-40 GPa). It is worth noting that the chemical bonds between the W layers and two different kinds of B layers show obvious polarization character based on the results obtained from X-ray photoelectron spectroscopy (XPS) and electron localization functions (ELFs), density of states (DOS), topological analysis of the static electron density and Mulliken population. This result can well clarify that WB2 is only a hard but not superhard material. Thus, a 3D network structure can not be formed between the W layers and the B layers which is previously predicted by theoretical calculations. Our results are helpful to understand the hardness mechanism and design superhard materials in TMBs.

PMID:
28295104
DOI:
10.1039/c6cp04287b

Supplemental Content

Full text links

Icon for Royal Society of Chemistry
Loading ...
Support Center