J Phys Chem Lett. 2015 May 21;6(10):1883-90. doi: 10.1021/acs.jpclett.5b00732. Epub 2015 May 6.

Bright Visible-Infrared Light Emitting Diodes Based on Hybrid Halide Perovskite with Spiro-OMeTAD as a Hole-Injecting Layer.

Author information

1
†Photovoltaic and Optoelectronic Devices Group, Departament de Física, Universitat Jaume I, 12071 Castelló, Spain.
2
‡Instituto de Energías Renovables, Universidad Nacional Autónoma de México, Apartado Postal 34, Temixco, Morelos 62580, México.

Abstract

Hybrid halide perovskites that are currently intensively studied for photovoltaic applications, also present outstanding properties for light emission. Here, we report on the preparation of bright solid state light emitting diodes (LEDs) based on a solution-processed hybrid lead halide perovskite (Pe). In particular, we have utilized the perovskite generally described with the formula CH3NH3PbI(3-x)Cl(x) and exploited a configuration without electron or hole blocking layer in addition to the injecting layers. Compact TiO2 and Spiro-OMeTAD were used as electron and hole injecting layers, respectively. We have demonstrated a bright combined visible-infrared radiance of 7.1 W·sr(-1)·m(-2) at a current density of 232 mA·cm(-2), and a maximum external quantum efficiency (EQE) of 0.48%. The devices prepared surpass the EQE values achieved in previous reports, considering devices with just an injecting layer without any additional blocking layer. Significantly, the maximum EQE value of our devices is obtained at applied voltages as low as 2 V, with a turn-on voltage as low as the Pe band gap (V(turn-on) = 1.45 ± 0.06 V). This outstanding performance, despite the simplicity of the approach, highlights the enormous potentiality of Pe-LEDs. In addition, we present a stability study of unsealed Pe-LEDs, which demonstrates a dramatic influence of the measurement atmosphere on the performance of the devices. The decrease of the electroluminescence (EL) under continuous operation can be attributed to an increase of the non-radiative recombination pathways, rather than a degradation of the perovskite material itself.

KEYWORDS:

external quantum efficiency; halide perovskite; light-emitting diodes; spiro-OMeTAD

Supplemental Content

Full text links

Icon for American Chemical Society
Loading ...
Support Center