One-Pot synthesized bicontinuous hierarchical Li3V2(PO4)3/C mesoporous nanowires for high-rate and ultralong-life lithium-ion batteries.

Author information

1
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, WUT-Harvard Joint Nano Key Laboratory, Wuhan University of Technology , Wuhan 430070, China.

Abstract

Lithium-ion batteries have attracted enormous attention for large-scale and sustainable energy storage applications. Here we present a design of hierarchical Li3V2(PO4)3/C mesoporous nanowires via one-pot synthesis process. The mesoporous structure is directly in situ carbonized from the surfactants (CTAB and oxalic acid) along with the crystallization of Li3V2(PO4)3 without using any hard templates. As a cathode for lithium-ion battery, the Li3V2(PO4)3/C mesoporous nanowires exhibit outstanding high-rate and ultralong-life performance with capacity retention of 80.0% after 3000 cycles at 5 C in 3-4.3 V. Even at 10 C, it still delivers 88.0% of its theoretical capacity. The ability to provide this level of performance is attributed to the hierarchical mesoporous nanowires with bicontinuous electron/ion pathways, large electrode-electrolyte contact area, low charge transfer resistance, and robust structure stability upon prolonged cycling. Our work demonstrates that the unique mesoporous nanowires structure is favorable for improving the cyclability and rate capability in energy storage applications.

PMID:
24437341
DOI:
10.1021/nl404709b

Supplemental Content

Full text links

Icon for American Chemical Society
Loading ...
Support Center