Photochem Photobiol. 2013 Sep-Oct;89(5):1047-56. doi: 10.1111/php.12136. Epub 2013 Aug 29.

Photocatalytic degradation of organic reactive dyes over MnTiO3/TiO2 heterojunction composites under UV-visible irradiation.

Author information

1
Department of Chemistry, Periyar University, Salem, India.

Abstract

In this study, the photocatalytic degradation of organic reactive dyes have been investigated using MnTiO3/TiO2 heterojunction composites in the presence of electron acceptors under UV-Visible light irradiation. This MnTiO3/TiO2 heterojunction composites were prepared by annealing different mass ratios of pyrophanite MnTiO3 (3-11 wt%) and TiO2 at 300°C. All the MnTiO3/TiO2 heterojunction composites were characterized by spectral techniques like X-ray diffraction (XRD), scanning electron microscope (SEM) and diffused reflectance UV-visible spectroscopic analysis (DRS). Among them, 9 wt% MnTiO3/TiO2 heterojunction composites exhibited higher photocatalytic activity for the degradation of Reactive Blue 4 (RB 4). The photocatalytic efficiency of 9 wt% MnTiO3/TiO2 heterojunction composites was further enhanced by the addition of substantial amount of electron acceptors like hydrogen peroxide (H2O2) and ammonium peroxydisulfate ([NH4]2S2O8). The presence of oxidants (electron acceptors) facilitates the fast degradation of dye solution even in higher concentration upto 200 mg/L. The photocatalytic activity of MnTiO3/TiO2 heterojunction composites was also studied for the degradation of other four different structured reactive dyes. The extent of mineralization of these organic reactive dyes during photocatalytic degradation was estimated from COD analysis. MnTiO3/TiO2 heterojunction composites was also found to have good photostability in the presence of oxidants.

PMID:
23848842
DOI:
10.1111/php.12136
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Wiley
    Loading ...
    Support Center