Effects of degumming conditions on electro-spinning rate of regenerated silk.

Author information

1
Department of Biomedical Engineering, Washington University, St. Louis, MO 63130, USA.

Abstract

Electro-spun silk webs are potentially good candidates as tissue engineering scaffolds owing to their good bio- and cyto-compatibility. However, the low fabrication rate of electro-spun silk mats has been one of the obstacles in the mass production of such nanofibrous silk mats in applications to the biomedical field. In this study, the effects of degumming ratio and silk concentration on the electro-spinning process were investigated by using regenerated silk with different residual sericin contents and different silk concentrations in terms of the morphology and structure of the electro-spun silk web. The rate of production of electro-spun silk mats could be increased by approximately 5 fold at a degumming ratio of 19.5%. The electro-spinning rate of silk was affected by two main factors: (1) dope solution viscosity and (2) degumming ratio of silk. The conductivity of the silk dope solution, however, had little effects on the electro-spinning of regenerated silk. A constant spun fiber morphology was observed within the electro-spinning rate range (0.3-1.4 ml/h). Fourier transform infrared spectroscopy showed that partial β-sheet crystallization occurred during electro-spinning. The molecular conformation was relatively unaffected by the electro-spinning rate of silk.

KEYWORDS:

Degumming condition; Electro-spinning rate; Regenerated silk

PMID:
23817099
DOI:
10.1016/j.ijbiomac.2013.06.039
[Indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Elsevier Science
    Loading ...
    Support Center