J Mech Behav Biomed Mater. 2013 Oct;26:43-53. doi: 10.1016/j.jmbbm.2013.05.021. Epub 2013 May 31.

Bioerodible calcium sulfate/poly(β-amino ester) hydrogel composites.

Author information

1
Center for Biomedical Engineering, Wenner-Gren Research Lab, University of Kentucky, Lexington, KY 40506-0070, USA.

Abstract

The capacity to quickly regenerate or augment bone lost as a result of resorption is crucial to ensure suitable application of prosthetics for restoring masticatory function. Calcium sulfate hemihydrate (CS)-based bone graft substitute composites containing poly(β-amino ester) (PBAE) biodegradable hydrogel particles were developed to act as a 'tenting' barrier to soft tissue infiltration, potentially providing adequate space to enable vertical bone regeneration. CS has long been recognized as an osteoconductive biomaterial with an excellent reputation as a biocompatible substance. Composite samples were fabricated with varying amounts (1 or 10 wt%) and sizes (53-150 or 150-250 μm) of gel particles embedded in CS. The swelling and degradation rates of PBAE gels alone were rapid, resulting in complete degradation in less than 24h, an important characteristic to aid in controlled release of drug. MicroCT images revealed a homogeneous distribution of gel particles within the CS matrix. All CS samples degraded via surface erosion, with the amount of gel particles (i.e., 10 wt% gel particles) having only a small, but significant, effect on the dissolution rate (4% vs. 5% per day). Compression testing determined that the amount, but not the size, of gel particles had a significant effect on the overall strength of the composites. As much as a 75% drop in strength was seen with a 10 wt% loading of particles. A pilot study using PBAE particles loaded with the multipotential drug curcumin demonstrated sustained release of drug from CS composites. By adjusting the amount and/or size of the biodegradable gel particles embedded in CS, mechanical strength and degradation rates of the composites, as well as the drug release kinetics, can be tuned to fabricate, multi-functional 'space-making' bone grafting substitutes.

KEYWORDS:

Biodegradable; Bioerodible; Bone regeneration; Calcium sulfate; Composite; Controlled release

PMID:
23811276
PMCID:
PMC3713170
DOI:
10.1016/j.jmbbm.2013.05.021
[Indexed for MEDLINE]
Free PMC Article
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Elsevier Science Icon for PubMed Central
    Loading ...
    Support Center