The major functions required for load-bearing orthopaedic implants are load-bearing and mechanical or biological fixation with the surrounding bone. Porous materials with appropriate mechanical properties and adequate pore structure for fixation are promising candidates for load-bearing implant material. In previous work, the authors developed a novel titanium (Ti) foam sheet 1-2mm thick by an original slurry foaming method. In the present work, novel Ti foam is developed with mechanical properties compatible with cortical bone and biological fixation capabilities by layer-by-layer stacking of different foam sheets with volumetric porosities of 80% and 17%. The resulting multilayer Ti foam exhibited a Young's modulus of 11-12GPa and yield strength of 150-240MPa in compression tests. In vitro cell culture on the sample revealed good cell penetration in the higher-porosity foam (80% volumetric porosity), which reached 1.2mm for 21 days of incubation. Cell penetration into the high-porosity layers of a multilayer sample was good and not influenced by the lower-porosity layers. Calcification was also observed in the high-porosity foam, suggesting that this Ti foam does not inhibit bone formation. Contradictory requirements for high volumetric porosity and high strength were attained by role-sharing between the foam sheets of different porosities. The unique characteristics of the present multilayer Ti foam make them attractive for application in the field of orthopaedics.
Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.