Nano Lett. 2012 Sep 12;12(9):4775-83. doi: 10.1021/nl302214x. Epub 2012 Aug 28.

Creation and control of two-dimensional electron gas using Al-based amorphous oxides/SrTiO₃ heterostructures grown by atomic layer deposition.

Author information

1
Department of Chemistry and Chemical Biology, Harvard University, Cambridge, Massachusetts 02138, United States.

Abstract

The formation of a two-dimensional electron gas (2-DEG) using SrTiO(3) (STO)-based heterostructures provides promising opportunities in oxide electronics. We realized the formation of 2-DEG using several amorphous layers grown by the atomic layer deposition (ALD) technique at 300 °C which is a process compatible with mass production and thereby can provide the realization of potential applications. We found that the amorphous LaAlO(3) (LAO) layer grown by the ALD process can generate 2-DEG (∼1 × 10(13)/cm(2)) with an electron mobility of 4-5 cm(2)/V·s. A much higher electron mobility was observed at lower temperatures. More remarkably, amorphous YAlO(3) (YAO) and Al(2)O(3) layers, which are not polar-perovskite-structured oxides, can create 2-DEG as well. 2-DEG was created by means of the important role of trimethylaluminum, Me(3)Al, as a reducing agent for STO during LAO and YAO ALD as well as the Al(2)O(3) ALD process at 300 °C. The deposited oxide layer also plays an essential role as a catalyst that enables Me(3)Al to reduce the STO. The electrons were localized very near to the STO surface, and the source of carriers was explained based on the oxygen vacancies generated in the STO substrate.

PMID:
22908907
DOI:
10.1021/nl302214x
[Indexed for MEDLINE]

Supplemental Content

Full text links

Icon for American Chemical Society
Loading ...
Support Center