Hybrid transparent electrodes of silver nanowires and carbon nanotubes: a low-temperature solution process.

Author information

1
The Institute of Scientific and Industrial Research (ISIR), Osaka University, Mihogaoka 8-1, Ibaraki, Osaka, 567-0047, Japan. takehiro_tokuno@eco.sanken.osaka-u.ac.jp.

Abstract

Hybrid transparent electrodes with silver nanowires (AgNWs) and single-walled carbon nanotubes (SWCNTs) were fabricated on plastic films by a low-temperature solution process. The hybrid transparent electrodes exhibited a sheet resistance of 29.2 Ω/sq with a transparency of 80% when 6 wt.% of SWCNTs was mixed with AgNWs. This sheet resistance was less than one-fourth that of the AgNW transparent electrodes that were prepared using the same method. This reduction in sheet resistance is because the SWCNTs formed bridges between the AgNWs, thus, resulting in high conductivity of the hybrid transparent electrodes. The hybrid electrodes formed on plastic films exhibited high conductivity as well as excellent stability in sheet resistance when tested using a repeated bending test.PACS: 62.23.Hj; 61.48.De; 81.15.-z.

PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Springer Icon for PubMed Central
    Loading ...
    Support Center