J Nanosci Nanotechnol. 2012 Feb;12(2):1440-3.

Microstructures and magnetic anisotropy of single-layered Fe-Pt alloy films by in-situ annealing.

Author information

1
Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu 30013, Taiwan.

Abstract

The single-layered Fe-Pt films with thickness of 30 nm are in-situ deposited directly on Si substrate at various substrate temperatures (Ts) of 350 to 590 degrees C. As the Fe-Pt film is sputtered at substrate temperature is 350 degrees C, it shows (111) preferred orientation and tends to in-plane magnetic anisotropy. The L1(0) Fe-Pt film with (001) texture is obtained and exhibited perpendicular magnetic anisotropy as the substrate temperature is increased to 470 degrees C. The perpendicular coercivity (Hc perpendicular), saturation magnetization (Ms) and perpendicular squareness (S perpendicular) of this film are 6.9 kOe, 674 emu/cm3 and 0.89, respectively, which reveal its significant potential as perpendicular magnetic recording media.

PMID:
22629974
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Loading ...
    Support Center