Nanoscale Res Lett. 2012 Jan 5;7:43. doi: 10.1186/1556-276X-7-43.

Visible emission from Ce-doped ZnO nanorods grown by hydrothermal method without a post thermal annealing process.

Author information

1
LED-IT Fusion Technology Research Center and Department of Electronic Engineering, Yeungnam University, Gyeongbuk, 712-749, Korea. jaehyun@dgist.ac.kr.

Abstract

Visible light-emitting Ce-doped ZnO nanorods [NRs] without a post thermal annealing process were grown by hydrothermal method on a Si (100) substrate at a low temperature of 90°C. The structural investigations of Ce-doped ZnO NRs showed that the Ce3+ ions were successfully incorporated into the ZnO lattice sites without forming unwanted Ce-related compounds or precipitates. The optical investigation by photoluminescence spectra shows that the doped Ce3+ ions in the ZnO NRs act as an efficient luminescence center at 540 nm which corresponds to the optical transition of 5d → 4f orbitals in the Ce3+ ions. The photoluminescence intensity of the Ce-doped ZnO NRs increased with the increasing content of the Ce-doping agent because the energy transfer of the excited electrons in ZnO to the Ce3+ ions would be enhanced by increased Ce3+ ions.

PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Springer Icon for PubMed Central
    Loading ...
    Support Center