ACS Nano. 2012 Jan 24;6(1):810-8. doi: 10.1021/nn204675r. Epub 2011 Dec 16.

The application of highly doped single-layer graphene as the top electrodes of semitransparent organic solar cells.

Author information

  • 1Department of Applied Physics and Materials Research Centre, The Hong Kong Polytechnic University, Hong Kong, China.

Abstract

A single-layer graphene film with high conductance and transparency was realized by effective chemical doping. The conductance of single-layer graphene was increased for more than 400% when it was doped with Au nanoparticles and poly(3,4-ethylenedioxythiophene): poly(styrene sulfonic acid). Then semitransparent organic solar cells based on poly(3-hexylthiophene) (P3HT) and phenyl-C61-butyric acid methyl ester (PCBM) were fabricated with single-layer graphene and indium tin oxide (ITO) as the top and bottom electrodes, respectively. The performance of the devices was optimized by tuning the active layer thickness and doping the single-layer graphene electrodes. The maximum efficiency of 2.7% was observed in the devices with the area of 20 mm(2) illuminated from graphene electrode under the AM1.5 solar simulator. It is notable that all of the devices showed higher efficiency from the graphene than ITO side, which was attributed to the better transmittance of the graphene electrodes. In addition, the influence of the active area of the organic solar cell on its photovoltaic performance was studied. We found that, when the active areas increased from 6 to 50 mm(2), the power conversion efficiencies decreased from 3% to 2.3% because of the increased series resistances and the decreased edge effect of the devices.

PMID:
22148872
DOI:
10.1021/nn204675r
[PubMed - indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for American Chemical Society
    Loading ...
    Support Center