Langmuir. 2011 Dec 6;27(23):14025-32. doi: 10.1021/la2021116. Epub 2011 Oct 28.

Effect of pH on the synthesis and properties of luminescent SiO2/calcium phosphate:Eu3+ core-shell nanoparticles.

Author information

1
Fraunhofer Institute for Silicate Research ISC, Neunerplatz 2, 97082 Würzburg, Germany. sofia.dembski@isc.fraunhofer.de

Abstract

A novel method for the synthesis of luminescent SiO(2)/calcium phosphate (CaP):Eu(3+) core-shell nanoparticles (NPs) was developed via a sol-gel route followed by annealing at a temperature of 800 °C. The object of this study was the investigation of the effect of pH on the formation of a CaP shell around the silica core. The resulting annealed NPs exhibited an amorphous SiO(2) core and a crystalline luminescent shell. The formation of a CaP layer was possible at pH below 4.5 and above 6.5 during the coating step. The crystal structure of the shell was studied by X-ray diffraction analysis. Hydroxyapatite (HAp) and α-tricalcium phosphate were detected as crystal phases of the surrounding layer. However, NPs produced under basic conditions exhibited a higher crystallinity of the CaP layer than did samples coated at pH below 4.5. In the pH interval between 4.5 and 6.5, no shell growth but the formation of secondary NPs containing CaO and Ca(OH)(2) was observed. Furthermore, SiO(2)/CP:Eu(3+) core-shell NPs were investigated by transmission electron microscopy, dynamic light scattering, Fourier transform infrared spectroscopy, inductively coupled plasma optical emission spectrometry, and photoluminescence spectroscopy. The resulting HAp-coated NPs were successfully tested by a cell-culture-based viability assay with respect to a later application as a luminescent marker for biomedical applications.

PMID:
21988231
DOI:
10.1021/la2021116
[Indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for American Chemical Society
    Loading ...
    Support Center