Eur J Oral Sci. 2011 Oct;119(5):395-400. doi: 10.1111/j.1600-0722.2011.00849.x. Epub 2011 Aug 5.

Influence of oxygen inhibition on the surface free-energy and dentin bond strength of self-etch adhesives.

Author information

1
Department of Operative Dentistry, Nihon University School of Dentistry, Tokyo, Japan.

Abstract

We compared the surface free-energies and dentin bond strengths of single-step self-etch adhesives with and without an oxygen-inhibited layer. The labial dentin surfaces of bovine mandibular incisors were wet ground with #600-grit silicon carbide paper. The adhesives were applied to the ground dentin, light-irradiated, and the oxygen-inhibited layer was either retained or removed with ethanol. The surface free-energies were determined by measuring the contact angles of three test liquids placed on the cured adhesives. The dentin bond strengths of specimens with and without the oxygen-inhibited layer were measured. For all surfaces, the value of the estimated surface tension component was relatively constant at 35.5-39.8 mJ m(-2) . The value of the , Lewis acid component increased slightly when the oxygen-inhibited layer was removed, whereas that of the , Lewis base component decreased significantly. The bond strengths of the self-etch adhesives were significantly lower in specimens without an oxygen-inhibited layer (13.2-13.6 MPa) than in those with an oxygen-inhibited layer (17.5-18.4 MPa). These results indicate that the presence of an oxygen-inhibited layer in single-step self-etch adhesives with advanced photoinitiators promotes higher dentin bond strength.

[Indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Wiley
    Loading ...
    Support Center