Hg(II) immobilized MWCNT graphite electrode for the anodic stripping voltammetric determination of lead and cadmium

The preparation of Hg(II)-modified multi walled carbon nanotube (MWCNT) by reaction of oxidized MWCNT with aqueous HgCl(2) was carried out. The Hg(II)-modified multi walled carbon nanotube (Hg(II)/MWCNT) dispersed in Nafion solution was used to coat the polished graphite electrode surface. The Hg(II)/MWCNT modified graphite electrode was held at a cathodic potential (-1.0 V) to reduce the coordinated Hg(II) to Hg forming nanodroplets of Hg. The modified electrode was characterized by FESEM/EDAX which provided useful insights on the morphology of the electrode. The SEM images showed droplets of Hg in the size of around 260 nm uniformly distributed on the MWCNT. Differential pulse anodic stripping voltammetry (DPASV) and electrochemical impedance spectroscopy were used to study the Hg(II) binding with MWCNT. Differential pulse anodic stripping voltammetry of ppb levels of cadmium and lead using the modified electrode yielded well-defined peaks with low background current under a short deposition time. Detection limit of 0.94 and 1.8 ng L(-1) were obtained following a 3 min deposition for Pb(II) and Cd(II), respectively. Various experimental parameters were characterized and optimized. High reproducibility was observed from the RSD values for 20 repetitive measurements of Pb(II) and Cd(II) (1.7 and 1.9%, respectively). The determination of Pb(II) and Cd(II) in tap water and Pb(II) in human hair samples was carried out. The above method of fabrication of Hg(II)/MWCNT modified graphite electrode clearly suggests a safe route for preparing Hg immobilized electrode for stripping analysis.