Opt Express. 2011 Mar 28;19(7):5802-10. doi: 10.1364/OE.19.005802.

Sculpturing of photonic crystals by ion beam lithography: towards complete photonic bandgap at visible wavelengths.

Author information

1
Centre for Micro-Photonics, Faculty of Engineering and Industrial Sciences Swinburne University of Technology, Hawthorn, VIC, Australia. SJuodkazis@swin.edu.au

Abstract

Three dimensional (3D) ion beam lithography (IBL) is used to directly pattern 3D photonic crystal (PhC) structures in crystalline titania. The process is maskless and direct write. The slanted pore 3D structures with pore diameters of 100 nm having aspect ratio of 8 were formed. It is shown that chemical enhancement of titania removal up to 5.2 times is possible in XeF2 gas for the closest nozzle-to-sample distance; the enhancement was ∼ 1.5 times for the actual 3D patterning due to a sample tilt. Tolerances of structural parameters and optimization of IBL processing required for the fabrication of PhCs with full photonic bandgap in visible spectral range in rutile are outlined. Application potential of 3D-IBL is discussed.

PMID:
21451604
[Indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Loading ...
    Support Center