Nat Nanotechnol. 2010 Oct;5(10):718-21. doi: 10.1038/nnano.2010.149. Epub 2010 Jul 25.

Reduction of thermal conductivity in phononic nanomesh structures.

Author information

1
Division of Chemistry and Chemical Engineering, MC 127-72 1200 East California Boulevard, California Institute of Technology, Pasadena, California 91125, USA.

Abstract

Controlling the thermal conductivity of a material independently of its electrical conductivity continues to be a goal for researchers working on thermoelectric materials for use in energy applications and in the cooling of integrated circuits. In principle, the thermal conductivity κ and the electrical conductivity σ may be independently optimized in semiconducting nanostructures because different length scales are associated with phonons (which carry heat) and electric charges (which carry current). Phonons are scattered at surfaces and interfaces, so κ generally decreases as the surface-to-volume ratio increases. In contrast, σ is less sensitive to a decrease in nanostructure size, although at sufficiently small sizes it will degrade through the scattering of charge carriers at interfaces. Here, we demonstrate an approach to independently controlling κ based on altering the phonon band structure of a semiconductor thin film through the formation of a phononic nanomesh film. These films are patterned with periodic spacings that are comparable to, or shorter than, the phonon mean free path. The nanomesh structure exhibits a substantially lower thermal conductivity than an equivalently prepared array of silicon nanowires, even though this array has a significantly higher surface-to-volume ratio. Bulk-like electrical conductivity is preserved. We suggest that this development is a step towards a coherent mechanism for lowering thermal conductivity.

PMID:
20657598
DOI:
10.1038/nnano.2010.149

Supplemental Content

Loading ...
Support Center