Guang Pu Xue Yu Guang Pu Fen Xi. 2010 Jan;30(1):270-3.

[XPS study on the influence of calcination conditions to cerium ion valence].

[Article in Chinese]

Author information

1
College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China. meiyan@bjut.edu.cn

Abstract

For the system of Ce(NO3)2.6H2O and urea solution during homogeneous precipitation method, X-ray diffraction (XRD), infrared spectrum (IR) and especially X-ray photoelectron spectroscopy (XPS) were used to study and characterize the product structure, variety of cerium ion valence, compound surface character and kernel electronic configurations. The results of XRD and IR showed that calcination temperature had a great effect on the cerium ion valence. The products are orthorhombic Ce2 O(CO3)2.H2O with valence III by using homogeneous precipitation method directly. When heated from the temperature 200 degrees C to 250 degrees C, the product of CeO(CO3)2.H2O with valence VI was finally changed into stable CeO2 with valence IV. XPS was used to study the surface character and kernel electronic configurations of the three different compounds through fine scanning of O(1s), Ce(3d) and Ce(4d) apices, and the results approved that the compounds with different valences are caused by the different valence electronic configurations of the products.

PMID:
20302130

Supplemental Content

Loading ...
Support Center