The results of assays carried out on plates used in the construction industry, manufactured entirely with solid wastes of a recycled paper plant, are presented and compared with the results obtained using agglomerated wood and plywood plates. Previous results had shown that wastes are composed essentially of polymers when these wastes are generated by recycled paper produced with the "waved type II" shavings. These solid wastes were placed in a mold that was heated and pressed with a hydraulic press in order to obtain the plates. The waste-produced plates were submitted to tests for humidity, swelling, water absorption, density, modulus of rupture-static bending, modulus of elasticity and direct screw withdrawal. These same assays had been carried out on two types of commercial wood plates, agglomerated wood and plywood, in order to compare the results with those obtained with the waste plate. Waste plates had similar behavior to the agglomerated wood plate, but it was possible to distinguish greater flexibility in the waste-produced plate and a significant difference in the tests for swelling and water absorption which showed the waste plate had a better performance than the agglomerated wood and plywood plates.