The current study evaluated the effect of 2% chlorhexidine digluconate (CHX) on the immediate and six-month resin-dentin bond strength (BS) and nanoleakage pattern (NL) of etch-and-rinse adhesives when applied in aqueous or associated to the phosphoric acid conditioner. The occlusal enamel of 42 caries-free extracted molars was removed in order to expose a flat dentin surface. In groups 1 and 2 (control-C), the surfaces were acid etched with conventional phosphoric acid, and the adhesives Prime&Bond NT (PB) and Adper Single Bond 2 (SB) were applied after rinsing, drying and rewetting with water. In groups 3 and 4 (Ac/CHX), the adhesives were applied in a similar manner, however, a 2% CHX-containing acid was previously applied. In groups 5 and 6 (CHX), the adhesives were applied according to the control group; however, the rewetting procedure was performed with an aqueous solution of 2% CHX for 60 seconds. Composite buildups (Opallis, FGM) were constructed incrementally, and the specimens were longitudinally sectioned in the "x" and "y" directions to obtain bonded sticks (0.8 mm2) to be tested in tension at 0.5 mm/minute immediately or after six months of water storage. For NL, two bonded sticks from each tooth were coated with nail varnish, placed in silver nitrate and polished down with SiC paper. Resin-dentin interfaces were analyzed by EDX-SEM. The BS and NL data from each adhesive was submitted to two-way repeated measures ANOVA and Tukey's test (alpha=0.05). After six months of water storage, significant reductions in BS were observed for both adhesives in the control group (p<0.05). When Ac/CHX or CHX was used, no significant reductions in BS were observed for both systems. Nanoleakage was more evident in the control group than in the experimental groups (p<0.05), even after six months. The use of CHX in an aqueous solution or associated with the acid conditioner was effective for reducing degradation of resin-dentin bonds after six months of water storage.