Biomed Mater. 2007 Jun;2(2):67-77. doi: 10.1088/1748-6041/2/2/003. Epub 2007 Mar 14.

Osteoblast proliferation on hydroxyapatite thin coatings produced by right angle magnetron sputtering.

Author information

  • 1Instituto Militar de Engenharia, IME, Rio de Janeiro, 22290-270, RJ, Brazil. mello@cbpf.br

Abstract

Right angle magnetron sputtering (RAMS) was used to produce hydroxyapatite (HA) film coatings on pure titanium substrates and oriented silicon wafer (Si(0 0 1)) substrates with flat surfaces as well as engineered surfaces having different forms. Analyses using synchrotron XRD, AFM, XPS, FTIR and SEM with EDS showed that as-sputtered thin coatings consist of highly crystalline hydroxyapatite. The HA coatings induced calcium phosphate precipitation when immersed in simulated body fluid, suggesting in vivo bioactive behavior. In vitro experiments, using murine osteoblasts, showed that cells rapidly adhere, spread and proliferate over the thin coating surface, while simultaneously generating strong in-plane stresses, as observed on SEM images. Human osteoblasts were seeded at a density of 2500 cells cm(-2) on silicon and titanium HA coated substrates by RAMS. Uncoated glass was used as a reference substrate for further counting of cells. The highest proliferation of human osteoblasts was achieved on HA RAMS-coated titanium substrates. These experiments demonstrate that RAMS is a promising coating technique for biomedical applications.

PMID:
18458438
DOI:
10.1088/1748-6041/2/2/003
[PubMed - indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for IOP Publishing Ltd.
    Loading ...
    Support Center