Effect of temperature and pipe material on biofilm formation and survival of Escherichia coil in used drinking water pipes: a laboratory-based study.

Author information

1
Institute of Environment and Resources, Technical University of Denmark, Bygning 115, 2800 Lyngby, Denmark. jsilhan@centrum.cz

Abstract

Segments of used drinking water pipes of galvanised steel (GS), cross-linked polyethylene (PEX), copper pipes (Cu) or new medium-density polyethylene (PE) were investigated for the formation of biofilm and survival of E. coli in biofilm and in the water phase. Pipes were filled with water and incubated at 15 degrees C or 35 degrees C under static conditions. Biofilm formation was followed during 32, 40 and 56 (58) d. The most dense biofilm was formed on GS, reaching approximately 4.7 x 10(5) CFU/cm2 measured as heterotrophic plate count (HPC), and at the other materials the density reached 3 x 10(3) CFU/cm2 on PE and PEX and 5 x 10(1) and 5 x 10(2) CFU/cm2 on Cu pipes after 58d at 15 degrees C. Biofilm HPC values were higher at 35 degrees C than at 15 degrees C, with only slightly higher values on the metals, but 100-fold higher on PE and PEX. Adenosine triphosphate (ATP) measurements confirmed the general trends observed by HPC. Higher temperature was seen to be an important factor reducing E. coli survival in the water phase in drinking water pipes. At 15 degrees C E. coli survived more than 4 d in GS and Cu pipes and 8 d in PE pipes, but was not detected after 48 h at 35 degrees C. The E. coli survived longer at both temperatures in the glass control bottles than in the drinking water pipes. Despite the obvious biofilm formation, E. coli was not detected in the biofilm at any of the investigated surfaces.

PMID:
17037132
[Indexed for MEDLINE]

Supplemental Content

Loading ...
Support Center