J Mater Sci Mater Med. 1999 Jul;10(7):401-9.

Interfacial bond strength of electrophoretically deposited hydroxyapatite coatings on metals.

Author information

1
School of Materials Science and Engineering, University of New South Wales, Sydney, NSW 2052, Australia.

Abstract

Hydroxyapatite (HAp) coatings were deposited onto substrates of metal biomaterials (Ti, Ti6Al4V, and 316L stainless steel) by electrophoretic deposition (EPD). Only ultra-high surface area HAp powder, prepared by the metathesis method 10Ca(NO3)2 + 6(NH4)2HPO4 + 8NH4OH), could produce dense coatings when sintered at 875-1000degreesC. Single EPD coatings cracked during sintering owing to the 15-18% sintering shrinkage, but the HAp did not decompose. The use of dual coatings (coat, sinter, coat, sinter) resolved the cracking problem. Scanning electron microscopy/energy dispersive spectroscopy (SEM/EDS) inspection revealed that the second coating filled in the "valleys" in the cracks of the first coating. The interfacial shear strength of the dual coatings was found, by ASTM F1044-87, to be approximately 12 MPa on a titanium substrate and approximately 22 MPa on 316L stainless steel, comparing quite favorably with the 34 MPa benchmark (the shear strength of bovine cortical bone was found to be 34 MPa). Stainless steel gave the better result since -316L (20.5 microm mK(-1)) > alpha-HAp (approximately 14 microm mK(-1)), resulting in residual compressive stresses in the coating, whereas alpha-titanium (approximately 10.3 microm mK(-1)) < alpha-HAp, resulting in residual tensile stresses in the coating.

PMID:
15348125
DOI:
10.1023/a:1008923029945

Supplemental Content

Loading ...
Support Center