The aim of this in vitro study was to compare the tensile bond strength of 3 different bonding systems, associated to composite resins, bonded to dentinal surfaces. Forty-four dentinal surfaces were obtained from recently extracted human molars. A standardized smear layer was obtained and the surfaces were divided in 3 groups: G1) self etch + microhybrid composite; G2) single-component adhesive + phosphoric acid + microhybrid composite and G3) conventional system (acid + primer + bond) + microhybrid composite. Specimens made of composite resin were constructed in the shape of an inverted truncated cone with 3 mm of diameter. Tensile bond strength test was performed at the speed of 0.5 mm/min, and the results were expressed in MPa. The analysis of variance ANOVA (p < 0.05) determined that the type of bonding system used influenced tensile bond strength. Tukey's test, however, showed that the results of the comparison between G2 and G3 were the only statistically significant ones, with G2 showing greater values of tensile bond strength.