Synthesis and Antibacterial Activity of Cationic Amino Acid-Conjugated Dendrimers Loaded with a Mixture of Two Triterpenoid Acids

To counteract the growing bacterial resistance, we previously reported the remarkable antimicrobial activity of amino acid-conjugated cationic dendrimers (CDs) against several Gram-negative species, establishing that the cationic lysine was essential for their potency. In this paper, CDs conjugated with lysine and arginine and encapsulating ursolic and oleanolic acids (UOACDs) were assumed to be excellent candidates for developing new antibacterial agents, possibly active against Gram-positive species. Indeed, both the guanidine group of arginine and the two triterpenoid acids are items known for directing antibacterial effects, particularly against Gram-positive bacteria. The cationic dendrimers were obtained by peripheral conjugation with the selected amino acids and by entrapping a physical mixture of the commercial triterpenoid acids. The cationic compounds were characterized and successfully tested against 15 Gram-positive isolates. Interesting minimum inhibitory concentration (MIC) values were obtained for all the dendrimer-drug agents, establishing that the antibacterial activity observed for the UOACDs strongly depended on the density and on the type of the cationic groups of the cationic amino acid-conjugated dendrimers and not on the presence and the release of UOA. Particularly, lysine was critical for potency, while arginine was critical for redirecting activity against Gram-positive species. Especially, a high cationic character, associated with a balanced content of lysine/arginine, produced a remarkable antimicrobial effect (MIC = 0.5–8.7 µM).


Introduction
The rapid and worldwide increase in antimicrobial resistance among bacterial pathogens, frequently associated with therapeutic failures and high mortality rates, urgently requires alternative curative options able to replace the no-longer-active antibiotics [1].
The most concern regards Gram-negative bacilli, such as Acinetobacter baumannii, Pseudomonas aeruginosa and Stenotrophomonas maltophilia, which are emerging as clinically relevant superbugs, contributing significantly, with their worrying resistance levels, to numerous therapeutic failures [2]. Today, antibiotic resistance has also become a major problem in the treatment of infections caused by many Gram-positive bacteria. The most important Gram-positive resistant organisms include penicillin-resistant Streptococcus pneumoniae, methicillin-resistant Staphylococcus aureus (MRSA), S. epidermidis (MRSE) and Enterococcal species, such as Enterococcus faecium and E. fecalis, that express high-level resistance to aminoglycosides and/or resistance to vancomycin (VRE) [3].
Frequently, these strains become tolerant to currently available agents, thus requiring innovative therapeutic strategies, including the use of alternative, nonconventional drugs, alone or in combination, and the development of new drugs. In particular, the prepared amino acid-conjugated dendrimer-drug systems possessed inner uncharged polyester matrices of the fourth (G4) or fifth (G5) generation (Figure 1b), peripherally esterified with mixtures having different contents of L-arginine (R) and Llysine (K) or with R alone. Additionally, they entrapped three, four or eight moles of UOA per mole of dendrimer. They were named G4R(16)K(19)UOA(4), G5R(38)K(30)UOA (8) and G5R(66)UOA(3), the numbers in round brackets being the contents of peripheral residues of amino acids conjugated for each dendrimer and the contents in equivalents of UOA entrapped per dendrimer mole. Their stylized structures have been represented in Figure 2, which also reports the number of moles of UOA loaded by one mole of each dendrimer.
Note that the final dendrimers retained a variable number of free hydroxyls during functionalization, which is indicated with the numbers subscripted close to the OH groups in Figure 2 and which contributed to their water solubility.   In particular, the prepared amino acid-conjugated dendrimer-drug systems possessed inner uncharged polyester matrices of the fourth (G4) or fifth (G5) generation (Figure 1b), peripherally esterified with mixtures having different contents of L-arginine (R) and Llysine (K) or with R alone. Additionally, they entrapped three, four or eight moles of UOA per mole of dendrimer. They were named G4R(16)K(19)UOA(4), G5R(38)K(30)UOA (8) and G5R(66)UOA(3), the numbers in round brackets being the contents of peripheral residues of amino acids conjugated for each dendrimer and the contents in equivalents of UOA entrapped per dendrimer mole. Their stylized structures have been represented in Figure 2, which also reports the number of moles of UOA loaded by one mole of each dendrimer.
Note that the final dendrimers retained a variable number of free hydroxyls during functionalization, which is indicated with the numbers subscripted close to the OH groups in Figure 2 and which contributed to their water solubility.  Note that the final dendrimers retained a variable number of free hydroxyls during functionalization, which is indicated with the numbers subscripted close to the OH groups in Figure 2 and which contributed to their water solubility.

Chemistry: Materials and Measurements
All the reagents and solvents were purchased from Merck (Darmstadt, Germany) and used without further purification. Ursolic acid (UA) and oleanolic acid (OA), with purity assessed by gas chromatography analysis, were purchased from Merck, Darmstadt, Germany (commercial cods. U6753 and O5504, respectively). The dialysis bags (D-Tube TM Dialyzer Maxi, MWCO 3.5 kDa) were purchased from Merck (Darmstadt, Germany). The solvents were dried and distilled according to standard procedures. Petroleum ether refers to the fraction with a boiling point of 40-60 • C. The uncharged dendrimer scaffolds G4 and G5 were prepared as previously described, and copies of the NMR spectra are available in the Supporting Information (SI) (Figures S1 and S2) [22]. Freeze-drying, centrifugations, HPLC analysis, thin-layer chromatography (TLC), flash chromatography (FC), elemental analyses, melting point analyses, FTIR and NMR spectroscopy of all the dendrimers, dynamic light scattering (DLS) analysis, Zeta potential determinations, and analysis of the in vitro release of UOA from the dendrimer complexes were performed on the instruments and with the same procedures previously reported [22,25,26]. Organic solutions were dried over anhydrous sodium sulfate and evaporated using a rotatory evaporator operating at a reduced pressure of about 1.3-2.7 kPa.
2.2. Synthesis of the Amino Acid-Conjugated Cationic Empty Dendrimers G4R(16)K (19), G5R(66) and G5R(38)K(30): General Procedure A solution of G4 or G5 in dry DMF (25 mg/mL) was added to a 1/1 feed molar ratio mixture of N-tert-butyloxycarbonyl (Boc)Arg(NO 2 ) and N-Boc-Lys or to N-BocArg(NO 2 ) (1.05 equiv./OH of G4 or G5) and DPTS (0.2 equiv./OH of G4 or G5), and treated with a solution of dicicloexylcarbodiimide (DCC) in CH 2 Cl 2 (54 mg/mL, 1.21 equiv./OH of G4 or G5). The solution was kept under magnetic stirring at room temperature for 24 h. The precipitated DCU was removed by filtration and washed with fresh acetone (30 mL). The filtrates and washings were combined, concentrated at reduced pressure, taken with the minimum quantity of acetone and filtered through a short silica gel column (h = 8 cm, φ = 2 cm) with the help of acetone (25 mL) to remove the last traces of DCU. The solvent was removed by evaporation at reduced pressure to produce solids, which were crushed with Et 2 O, filtered and washed again with fresh Et 2 O to obtained spongy white solids, which were brought to constant weight under vacuum to produce the Boc-protected empty dendrimers, which were subjected to the following deprotection reaction. A solution of Boc-protected dendrimers freshly prepared in 8.8% HCOOH in methanol (35 mg/mL) was added to a slurry of 10% Pd/C (weight of catalyst/weight of substrate = 1/1) in 8.8% HCOOH in methanol (20 mg/mL) and stirred at room temperature overnight. The slurry was then filtered through a silica plug (h = 8 cm, φ = 2 cm) to remove the catalyst, which was washed with fresh methanol (30 mL). The filtrate and washings were combined and evaporated at reduced pressure to remove the solvent. The crude product was dissolved in dry methanol (6 mL) and treated under stirring at room temperature for 24 h with an excess of acetyl chloride (350 µL). After the removal of the solvent at reduced pressure, the solid residue was washed in excess acetone under stirring for 3 h, separated from the solvent by decantation and brought to constant weight at reduced pressure. The unprotected dendrimers were obtained as hydrochloride salts and were further purified by dissolution in water (5-10 mL), centrifugation (3400 rpm, 15 min) to remove impurities, and lyophilization. They were stored in a dryer on P 2  Exactly weighed amounts of UO (500 mg, 1.09 mmol) and of OA (500 mg, 1.09 mmol) were transferred into a mortar. Then, by using the pestle of the mortar, the two solids were carefully mixed, obtaining a fine dispersion, which was furtherly homogenized in a mixer. The mixture obtained was characterized by NMR analysis, which confirmed the 1:1 ratio of the two constituents.

Preparation of UOA-Loaded Dendrimers (UOACDs): General Procedure
A solution of dendrimers in dry MeOH (2.0 mg/mL) was added to the UOA 1:1 physical mixture (9 equiv.) of commercial UA and OA. The solution was kept under vigorous magnetic stirring at room temperature for 72 h in the dark. Then, after the removal of the solvent at reduced pressure, the obtained white solids were suspended in dichloromethane (DCM) overnight to wash away the free UOA not entrapped. The solids not dissolved were decanted; the DCM was separated and evaporated to obtain a white solid identified as UOA by IR analysis.
The residual solids were brought to constant weight and then dissolved in MeOH/H 2 O and precipitated in acetone in a centrifuge tube. After two cycles of centrifugation (3400 r/min) and washings with acetone, the wet solids were brought to constant weight under reduced pressure and then stored on P 2 O 5 in a dryer. The physicochemical properties and spectral data of the obatained G4 and G5 UOACDs are reported in Table 1.

Microorganisms
A total of 17 isolates, comprising two strains of clinical Gram-negative bacteria and 15 isolates belonging to 4 Gram-positive species, were used in this study. The gram-positive bacteria included 12 strains of clinical origin and 3 of marine origin, isolated from seawater of the Ligurian west coast. All the isolates were identified with a VITEK ® 2 (Biomerieux, Firenze, Italy) or the matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometric technique (Biomerieux, Firenze, Italy). Of the tested organisms, 2 strains were of the Enterobacteriaceae family (one E. coli and one K. pneumoniae resistant (KCP)); 6 strains belonged to the Staphilococcus genus, including 2 methicillin-resistant S. auresus (MRSA) and one susceptible, and 2 methicillin-resistant S. epidermidis (MRSE) and one susceptible; and 9 strains were of the Enterococcus genus (4 E. faecalis resistant to vancomycin (VRE), including strains 19 and 51 of marine origin, and one susceptible, and 3 E. faecium VRE, including strain 3 of marine origin, and one susceptible).

Antimicrobial Assays
The minimal inhibitory concentrations (MICs) of the three UOACDs, UOA and three empty dendrimers on the pathogens were determined following the microdilution procedure detailed by the European Committee on Antimicrobial Susceptibility Testing EU-CAST [27].
Briefly, overnight cultures of bacteria were diluted to yield standardized inocula of 1.5 × 10 8 colony-forming units (CFU)/mL. Aliquots of each suspension were added to 96-well microplates containing the same volumes of serial 2-fold dilutions (ranging from 1 to 1024 µg/mL) of each dendrimer to yield a final concentration of about 5 × 10 5 cells/mL. The plates were then incubated at 37 • C. After 24 h of incubation at 37 • C, the lowest concentration of dendrimer that prevented visible growth was recorded as the MIC. Concerning these early investigations, all the MICs were obtained in triplicate, the degree of concordance was 3/3 in all the experiments, and the standard deviation (±SD) was zero.

Statistical Analysis
Data are expressed as means ±SDs. Concerning the MIC values, the experiments were performed in triplicate, the concordance degree was 3/3, and the ±SD was zero.

Positively Charged Amino Acid-Conjugated Dendrimer-Drug Compounds Designed for This Study
Concerning the idea of encapsulating UOA, it was thought that the presence of moieties of these triterpenoid acids, reported to be active against species belonging to the genera Staphylococcus and Enterococcus [28,29], could be helpful in achieving our goal. Moreover, note that by encapsulating the UOA mixture in the cationic dendrimers, we were successful in solubilizing the water-insoluble UA and OA, otherwise not bioavailable and, even if active in vitro, not administrable in vivo. Interestingly, in view of a future possible clinical use of these materials, their water solubility will instead allow an easy in vivo administration.
Regarding the design of the chemical structures of the dendrimer scaffolds, we made the following considerations. In the sector of antibacterial cationic dendrimers, and particularly of those modified with amino acids, high generations translate into a high multivalence, a high content of amino acids and, therefore, a high density of cationic charge [9,18,21,30]. A high cationic charge is an essential requirement for the interaction of the compounds with bacterial membranes and for them exerting their harmful action on these structures vital for pathogenic microorganisms, simply on contact. Consequently, two out of the three dendrimers were prepared to be of the fifth generation (G5), using, as functionalizing molecules, amino acids with two amino groups; in our case, this would have meant a high number of cationic groups. In addition, since in our previous study, G5 dendrimers containing lysine and histidine turned out to be highly selective for nonfermenting Gram-negative species, firstly, we decided to change the amino acid that proved to contribute little to the antibacterial activity (histidine) with arginine.
Secondly, we decided to also prepare a lower generation (G4) dendrimer, to explore whether a significantly reduced content of cationic groups and a less sharp cationic character could allow for the maintenance of significant antibacterial activity and could help to redirect it towards pathogens with a lower negative charge on the external layers, as happens in Gram-positive species. Since lysine was previously found to be essential for good antibacterial activity [21], we decided to maintain it as a functionalizing molecule in the dendrimers of the fourth and in one of the fifth generation and to associate lysine with arginine. Since the guanidine group present in the structure of arginine, at physiologic pH, provides guanidinium groups, which are reported to be more effective against Gram-positive than against Gram-negative bacteria [8,9], the presence of arginine in place of histidine would have helped to obtain antimicrobial agents active against Gram-positive bacterial strains. Finally, to evaluate the intrinsic efficiency of arginine, the second G5 dendrimer was functionalized exclusively with arginine.
Finally, we highlight that the three UOACDs of this paper were obtained without using UOA extracted from plants, but using a physical mixture of UO and OA purchased from Merck. The mixture was artificially prepared with the aim of reproducing the one commonly provided by the nature, in which UO and OA are in the ratio of 1:1.

Positively Charged Amino Acid-Conjugated Empty Dendrimers
For the preparation of the fourth-and fifth-generation dendrimers containing arginine and lysine residues, the grafting of amino acids was successful with DCC and DPTS as the activator and catalyst, respectively, instead of EDC and DMAP as frequently suggested. The analysis of the 1 H NMR spectra of both the Boc-protected intermediates and final cationic dendrimers evidenced that not all the OH groups at the periphery were reactive towards the protected amino acids, and a number of free hydroxyl groups were detected in all the compounds. By the integration and comparison of opportunely selected proton signals, it was possible to obtain the number of residual OH groups and the contents of amino acids of the Boc-protected forms of the three dendrimers. The deprotection of the Boc-dendrimer intermediates was performed in two consecutive steps by removing, first, the NO 2 group with formic acid in the presence of Pd/C, followed by treatment with CH 3 COCl and methanol to remove the Boc groups. The composition of amino acids and the number of residual OHs were obtained from the integrals of opportunely selected proton signals in the 1 H NMR spectra.
The results confirmed the previous data obtained for the Boc-protected compounds, and were employed to calculate the molecular weights (MW) of the dendrimers and the reaction yields. As an example, in the SI, an image is reported, which shows the spectral modifications that occurred both in the phase of esterification and in the phase of protecting-group removal, during the preparation of the cationic empty dendrimer G5R(38)K(30)OH (28), indicating the signals whose integrals were used to calculate its peripheral composition ( Figure S3). A similar scenario was also observed for the other two dendrimers.
The polycationic dendrimers ( Figure S4, SI) were obtained as hygroscopic glassy solids after freeze-drying and were soluble in MeOH, DMSO, DMF, and H 2 O and insoluble in toluene, Et 2 O, THF, dioxane, CH 2 Cl 2 , CHCl 3 , EtOAc, acetone, acetonitrile and EtOH. In addition, in order to have additional evidence of the prepared structures and of the composition at the periphery, the MWs of the cationic dendrimers were obtained experimentally, by the titration of amine hydrochlorides with HClO 4 solutions in AcOH in the presence of mercuric acetate and quinaldine red as an indicator [22,25]. The method is simple and low cost, and its accuracy was secured by a sharp endpoint of titration, while its reliability has been demonstrated by the reproducibility of its results [22,25].
The particle hydrodynamic size (diameter) and zeta potential of the prepared dendrimers were determined by dynamic light scattering (DLS) analysis. As expected, the mean diameter of the fourth-generation sample was lower than that of the fifth-generation ones, and also depended on the type of amino acid present on the periphery. They were 4.6, 5.1 and 5.3 nm, respectively, for G4R(16)K (19), G5R(66) and G5R(38)K(30), and comparable to the diameters reported for NH 2 dendrimers of the same generation [22]. The surface charge was positive (+34.8, +50.0 and +51.8 mV) and in perfect agreement with data reported in the literature for G4 and G5-PAMAM-NH 2 dendrimers. They showed higher values for the G5 samples than G4, increased with an increase in N (the number of cationic groups) and, being higher than the critical value of 30 mV, should assure a good stability in solution.

Physical Mixture of Commercial UA and OA, 1:1 (UOA)
The desired mixture, 1:1, was obtained by homogenizing, both manually and mechanically, UA and OA, and was analyzed by the NMR technique to establish its actual ratio. The 1 H NMR spectrum, recorded in CD 3 OD/DMSO-d6, confirmed the 1:1 ratio.

Preparation of Dendrimers Loaded with the Physical Mixture of UA and OA, 1:1 (UOA)
The UOACDs prepared in this study are original antibacterial cationic agents, because in place of using commercially available highly cationic and non-biodegradable PAMAM scaffolds, as host macromolecules for the transport and delivery of UOA, they were totally synthesized in our laboratory and harmonized hydrolysable ester-based uncharged matrices, with cationic shells made of natural amino acids. Note that, in view of a clinical use of the prepared compounds, the biodegradability of the uncharged dendrimer architectures should assure a minor risk of permanent damage to the cellular membranes of mammalian cells and minor toxicity.
Robust and optimized synthetic procedures were performed to prepare the UOAloaded polyester-based amino acid-conjugated cationic dendrimers as described in detail in Section 2.
Concerning the complexation reaction, it can be rationally assumed that the UOA mixture could be entrapped due to the presence of the several amino groups, capable of establishing hydrogen bonds and/or electrostatically interacting with the weak triterpenoid acids. In this regard, the literature reports that in dendrimer/drug systems [31][32][33], such as cationic PAMAM/weakly acidic drug moieties (ibuprofen, DOX, and MTX) [34][35][36], noncovalent forces, such as hydrogen bonding and ionic interactions, are among those mechanisms suggested to play a decisive part in dendrimer/drug complexation. The certainty that UOA was actually adsorbed/encapsulated in the cationic dendrimers and not simply physically mixed was ensured by the purification procedures for the UOACDs. In this regard, as described in the experimental part (Section 2.4), the crude solids obtained at the end of the encapsulation reaction were washed with DCM overnight to eliminate the still-free UOA fraction, which was then recovered by the washings and identified by FTIR.
As for the physicochemical characterization of G4R(16)K(19)UOA(4), G5R(38)K(30)UO A(8) and G5R(66)UOA(3), several techniques, including FTIR and NMR analysis, were employed to confirm the structures and to establish the number of UOA molecules that were entrapped in the dendrimer's structure. In addition, the MW values, particle sizes and Z-potentials, as well as the profiles of the release of UOA from the hosting dendrimers, were determined. Table 2 reports the main structural characteristics of the prepared UOACDs and their physicochemical properties, which were determined on the same instruments and following the same procedures previously described [26]. In particular, FTIR was not significantly diagnostic enough to confirm the formation of the complexes, but 1 H NMR spectroscopy was useful for having both qualitative and quantitative information about the composition of the prepared compounds.
As an example, in Figure 3, the 1 H NMR spectrum of G4R(16)K(19)UOA(4) is shown. The spectra of the other two UOACDs are available in the SI (Figures S5 and S6).
The peaks under 1.0 ppm, not present in the parent dendrimer spectrum ( Figure S7 in SI) and belonging to the UOA mixture, correspond to the seven CH 3 groups and H (C(5)) of UA and UO, for a total of 22 H [37], while the broad peak at 3.7 ppm and not present in the UOA spectrum ( Figure S7, SI) corresponds to the methylene in the CH 2 OH groups of the dendrimer. The peaks under 1.00 ppm and the broad peak around 3.7 ppm were very diagnostic for confirming the success of the encapsulation reaction, and the integral values associated with these peaks were used to estimate the numbers of UOA units encapsulated per dendrimer mole of all the compounds. Briefly, the numbers of UOA units per complex mole were obtained by comparing the integral values of the CH 2 OH groups of the dendrimer scaffolds at 3.6-3.8 ppm, which were associated with 13, 60 and 56 proton atoms for G4R (16) In particular, FTIR was not significantly diagnostic enough to confirm the formation of the complexes, but 1 H NMR spectroscopy was useful for having both qualitative and quantitative information about the composition of the prepared compounds.
As an example, in Figure 3, the 1 H NMR spectrum of G4R(16)K(19)UOA(4) is shown. The spectra of the other two UOACDs are available in the SI (Figures S5 and S6). The peaks under 1.0 ppm, not present in the parent dendrimer spectrum ( Figure S7 in SI) and belonging to the UOA mixture, correspond to the seven CH3 groups and H (C(5)) of UA and UO, for a total of 22 H [37], while the broad peak at 3.7 ppm and not present in the UOA spectrum ( Figure S7, SI) corresponds to the methylene in the CH2OH groups of the dendrimer. The peaks under 1.00 ppm and the broad peak around 3.7 ppm were very diagnostic for confirming the success of the encapsulation reaction, and the integral values associated with these peaks were used to estimate the numbers of UOA units encapsulated per dendrimer mole of all the compounds. Briefly, the numbers of UOA units per complex mole were obtained by comparing the integral values of the CH2OH groups of the dendrimer scaffolds at 3.6-3.8 ppm, which were associated with 13, 60 and 56 proton atoms for G4R (16)  As expected, among the dendrimers containing both L-lysine and L-arginine, the one of the fifth generation showed a better efficiency in complexing UOA, due to its larger number of cationic groups, which dictated a greater possibility for electrostatic interactions and the formation of hydrogen bonds.
Surprisingly, the dendrimer containing only L-arginine, although of the fifth generation and with a high number of cationic groups, showed very poor ability for trapping UOA, which was lower than that of G4R(16)K(19)UOA(4), which only had 70 cationic groups. These findings established that not only the number of cationic groups but also the type of cationic groups could influence the encapsulation ability. The estimated UOA units loaded per dendrimer mole were useful for estimating the MWs of the prepared UOACDs (Table 2). In particular, after having estimated the UOA units loaded per dendrimer mole, it was possible to make an estimate of the MWs of the compounds by simply summing the MWs of the forerunner dendrimers with the MWs of the UOAs multiplied by the numbers of complexed units as deduced from the NMR spectra. Since agents aimed at future clinical applications have to possess peculiar requisites, in terms of water solubility, particle dimensions and surface charges, the determination of their values and a brief discussion of the results obtained is herein mandatory. The particle sizes of the UOACDs ranged from 16 to 25 nm, while the Z-potentials were positive and ranged from 25 to 34 mV. It is known that small particles assure minor tissue toxicity, but extremely minute particles could easily undergo hepatobiliary and renal clearance [36]. A correct balance to minimize both tissue toxicity and fast clearance by the mononuclear phagocytic system (MPS) is the best solution, and, as reported, particles less than 100 nm and greater than 20 nm in size could be a good choice [38,39].
The average particle size of the UOACDs was, in any case, less than 100 nm, thus assuring that during a possible in vivo administration, they would not generate administration embolism, thus also being suitable for intravenous or intraperitoneal administration to the patient. Unfortunately, the G5R(66)UOA(3) particles displayed a mean size < 20 nm, and the short circulation time could affect their efficiency in vivo. The surface charge of the UOACDs had higher values for the G5 samples and increased with an increase in the number of cationic groups. The UOACDs displayed high water solubility, providing solutions stable over time, as shown by Z-potential values around 30 mV.
Since to explicate their pharmacological effects, entrapped drugs need to be released from the reservoir, the in vitro profile of UOA release from the prepared compounds was studied in buffer solutions at pH = 7.4, adding to the incubation medium ethanol, 20% v/v, to favor its solubility. Aliquots were taken out of the medium at fixed time points (1, 2, 5, 10, 24 and 48 h), the released triterpenoid acids were quantified by HPLC, and the results are reported as micrograms of UOA released from 10 mg of UOACD as a function of time in Figure S8 in the SI [26]. As the data shown in Figure S6 in the SI highlight, all the profiles of the drugs released from the cationic dendrimers showed a three-phase pattern. The first phase was resolved after the first hour of incubation at pH = 7.4, when the release was almost null. Then, a very fast release phase started, while after five hours, a sustained release phase took place. The amount of UOA released from the G4-UOA dendrimer was more than that released from the G5-UOA ones, and the release profile showed a dependence on the N value, due to the stronger interactions of the free UOA mixture with dendrimers having more cationic groups.

Antimicrobial Activities of G4R(16)K(19), G5R(38)K(30) and G5R(66)
The MIC values for all the three dendrimers were obtained by analyzing a total of 17 strains including 14 isolates of clinical derivation and 3 of marine origin. From the preliminary results obtained for E. coli and K. pneumoniae, selected as representatives of Gram-negative bacteria, it was established that CDs loaded with UOA were not effective in inhibiting their growth. For this reason, their activity was studied in more depth against Gram-positive species, towards which significant inhibitory properties have been reported, especially against 15 strains, representatives of the genera Enterococcus and Staphylococcus (Table 3). In this regard, it was considered essential to establish whether the antibacterial activity exerted by the dendrimer complexes was due to a synergistic activity of the UOA with the cationic dendrimers, to only the cationic dendrimers or to the UOA released. Rational speculations were possible by simply comparing the MIC values of the free UOA, the MIC values displayed by the UOACDs and the maximum concentrations of UOA obtainable from these antibacterial agents based on the observed MIC values ( Table 3). The maximum concentrations of UOA obtainable were calculated considering the UOA released after 24 h from 10 mg of each UOACD (Table 2). Interestingly, it can be asserted that the cationic amino acid-conjugated dendrimers themselves possessed antibacterial activity, that the presence of UOA did not contribute to the observed antibacterial potency, and that the inhibitory activity reported for the UOACDs was solely due to the cationic structures. Indeed, the data obtained showed that, with the exception of one isolated case, the maximum concentration of UOA obtainable on the basis of the MIC values reported (Table 3) was far below the concentrations of free UOA (MIC values of free UOA, Table 3) necessary to inhibit bacteria. For having an experimental confirmation of this speculation, the antibacterial activities of the cationic empty dendrimers were also evaluated against the same bacterial strains in the same conditions, and the results are reported in Table 4. While the MIC values observed were identical to those displayed by the correspondent UOACDs when expressed in µg/mL, when expressed in µM, even if no substantial differences were observed, the MIC values of the empty dendrimers were slightly higher, due to the low MWs of the samples. However, these findings did not establish that dendrimers could also be active at lower micromolar concentrations, which we could not observe, due to the serial 2-fold dilution method adopted to measure the MICs. Evidence supporting this hypotesis was obtained by administering to all the strains the micromolar concentrations observed for the MICs of the UOACDs, and a mainained inhibition of the bacterial growth was detected, thus confirming that the antibacterial activity displayed by the complexes was attributable to the cationic dendrimers only. Furthermore, by a comparison of the overstimated MIC values (µM) displayed by the empty dendrimers with those of commercial antibiotics, the MICs of the G4 and G5 CDs against the MDR bacteria of all the species turned out to be far lower than those of the considered antibiotics, thus asserting the high potency of our antibacterial agents against resistant species. In particular, G5R(66)UOA (3), containing only arginine, showed a similar potency against Enterococci and Staphylococci, exhibiting comparable MIC values, with a very narrow distribution, towards both the genera. Its activity against Staphylococci was lower than that of G5R(38)K(30)UOA (8), but with the exception of S. epidermidis 119, for which it was higher than that of G4R(16)K(19)UOA(4), probably due to the lower density of the cationic charge of the last dendrimer (70 cationic groups versus 132). On the contrary, against all the Enterococci, G5R(66)UOA(3) showed much lower antibacterial potency than both the G4RK dendrimer (less cationic) and the G5RK dendrimer (with a similar cationic charge). From these findings, it can be concluded that the genus Staphylococcus was more susceptible to the density of the cationic groups present in the dendrimer structure, while the genus Streptococcus was more susceptible to the presence of L-lysine.
The greatest antimicrobial activity of all the antibacterial agents was observed against the S. epidermidis 127 (MRSE) strain, which was the most susceptible isolate of the genus Staphylococcus to all the UOACDs, with an order of potency of G5R (38) It is noteworthy that the antibacterial activity of these cationic dendrimers was evident against susceptible genera, regardless of the patterns of resistance to current antibiotics of the isolates evaluated. Moreover, it can be stated that the antimicrobial activity of the herein-developed cationic materials depended mainly on the density of their cationic charge (and therefore on the number of cationic groups) and on the type of peripheral amino acids (i.e., on the type of ammonium group responsible for the cationic character). From the MIC values reported in Table 3, it appears that, against the genus Staphylococcus, the antibacterial activity of the UOACDs was proportional to the number of their cationic groups, while against the genus Enterococcus, good antibacterial activity was due to the presence of the cationic groups of lysine. Indeed, G5R(66)UOA (3), not containing lysine, although possessing a number of cationic groups comparable to that of G5R(38)K(39)UOA(8), showed much lower antibacterial activity against all the isolates of the genus Enterococcus (MIC values up to 37 times lower). Moreover, G4R(16)K(19)UOA(4), despite possessing a far lower number of cationic groups than G5R(66)UOA(3), was significantly more active against all the Enterococcus strains analyzed, probably due to the presence of lysine. Finally, since these first results show that all the dendrimer complexes were ineffective against the Gram-negative strains considered, it can be established that the presence of the arginine guanidine group contributed to making the GCDs selective, in particular, for the Gram-positive species.
In conclusion, we have identified new and unconventional antimicrobial agents that, being specifically active against the main and alarming species of Gram-positive bacteria, could replace traditional antibiotics usually employed against Staphylococci and Enterococci, including oxacillin and vancomycin, today ineffective against such multiresistant strains.
More in-depth investigations, such as time-killing experiments and turbidimetric studies, are underway to better characterize the activity of the developed CDs and to unveil their mechanisms of action at the molecular level.
In the unloaded dendrimer, the signal of the CH 2 OH group appears slightly shifted due to the different solvents used during spectrum acquisition. Figure S8. Profile of UOA release from UOACDs.

Author Contributions:
The authors A.M.S., G.C.S. and S.A. contributed equally to the conceptualization, methodology, software, validation, formal analysis, investigation, resources, data curation, writing-original draft preparation, writing-review and editing, and project administration for the present work. All authors have read and agreed to the published version of the manuscript.