Eur J Oral Sci. 2015 Jun;123(3):215-9. doi: 10.1111/eos.12181. Epub 2015 Mar 23.

Discrepancies in marginal and internal fits for different metal and alumina infrastructures cemented on implant abutments.

Author information

  • 1Department of Restorative Dentistry, School of Dentistry, Federal University of Pelotas, Pelotas, RS, Brazil.


Cemented crowns are increasingly being used on dental implants instead of on screw-retained prostheses because of the reliability of internal Morse taper implant-abutment connections. However, there is a lack of information on the fit of metal ceramic and premachined alumina infrastructures. Therefore, the aim of this study was to evaluate the marginal and internal fits of different metal and alumina infrastructures cemented on universal post abutments. A total of 45 abutments (6 mm in height and 3.3 mm in diameter) were divided into five groups on the basis of their infrastructure material: cobalt-chromium (CoCr), nickel-chromium (NiCr), nickel-chromium-molybdenum-titanium (NiCrMoTi), gold (Au), and premachined alumina. The alumina group showed marginal overextension, and the Au group showed the highest discrepancy in marginal fit among the metal alloys. The CoCr and alumina groups showed the lowest discrepancies in internal fit. In conclusion, the alumina cylinders exhibited the best internal fit, despite their horizontal overextension. Among the metal alloys, CoCr exhibited the best fit at critical regions, such as the cervical and occlusal areas.

© 2015 Eur J Oral Sci.


dental implants; dental internal fit; dental marginal adaptation; metal ceramic alloys; prosthesis