Matrix damage and chondrocyte viability following a single impact load on articular cartilage.

Author information

  • 1Department of Orthopaedics, University of Aberdeen, Foresterhill, Scotland, United Kingdom.

Abstract

An impact load was applied to full-depth circular samples of articular cartilage in vitro and the effects of impact energy and velocity on matrix integrity and chondrocyte viability were studied. Following a severe impact, calculated to correspond to the energy density over the cartilage surface that might be expected in a man jumping off a 1-m-high wall, the tissue was grossly disrupted. It became elliptical, fissured, and flattened. Cartilage samples remaining attached to the underlying bone showed less damage at similar drop masses and heights. Chondrocyte viability was found to decrease linearly with increasing impact energy. Cartilage biopsies maintained in culture for up to 15 days following impact gained mass over the first 3 days which they did not subsequently lose. The gain in mass increased with the severity of impact and was due to an increased hydration of the tissue. Scanning electron microscopy and light microscopy showed fissures penetrating the tissue but which were never found to pass through the full depth. They were commonly oriented at about 45 degrees to the plane of the surface and gave the appearance of being deflected parallel to the surface on reaching the transition zone. This produced a "delaminating" effect where the surface zone was separating from the deep zone.

PMID:
7574698
[PubMed - indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Elsevier Science
    Loading ...
    Write to the Help Desk