Pd-Enriched-Core/Pt-Enriched-Shell High-Entropy Alloy with Face-Centred Cubic Structure for C₁ and C₂ Alcohol Oxidation

High-entropy alloy nanoparticles (HEA NPs) have aroused great interest globally with their unique electrochemical, catalytic, and mechanical properties, as well as diverse activity and multielement tunability for multi-step reactions. Herein, a facile low-temperature synthesis method at atmospheric pressure is employed to synthesize Pd-enriched-HEA-core and Pt-enriched-HEA-shell NPs with a single phase of face-centred cubic structure. Interestingly, the lattice of both Pd-enriched-HEA-core and Pt-enriched-HEA-shell enlarge during the formation process of HEA, with tensile strains included in the core and shell of HEA. The as-obtained PdAgSn/PtBi HEA NPs show excellent electrocatalytic activity and durability for methanol oxidation reaction (MOR) and ethanol oxidation reaction (EOR). The specific (mass) activity of PdAgSn/PtBi HEA NPs for MOR is 4.7 mA cm^-2 (2874 mA mg_(Pd+Pt) ^-1 ), about 1.7 (5.9) and 1.5 (4.8) times higher than that of commercial Pd/C and Pt/C catalysts, respectively. Additional to high-entropy effect, Pt sites and Pd sites on the interface of the HEA act synergistically to facilitate the multi-step process towards EOR. This study offers a promising way to find a feasible route for scalable HEA manufacturing with promising applications.