Influence of CAD/CAM Milling and 3D-Printing Fabrication Methods on the Mechanical Properties of 3-Unit Interim Fixed Dental Prosthesis after Thermo-Mechanical Aging Process

This study assessed the influence of CAD/CAM milling and 3D-printing fabrication methods on mechanical properties of 3-unit interim fixed dental prosthesis (IFDPs) after thermo-mechanical aging. Forty 3-unit IFDPs were fabricated on a mandibular right second premolar and second molar of a typodont cast. Samples were fabricated from the following materials; auto-polymerized polymethyl methacrylate (conventional resin), CAD/CAM PMMA (milled resin) and two different CAD/CAM 3D-printed composite resins; digital light processing Asiga (DLP AS) and stereolithography NextDent (SLA ND). Mechanical properties were compared between the studied materials using Kruskal−Wallis test, followed by multiple pairwise comparisons using Bonferroni adjusted significance. There was a significant difference in flexural strength and microhardness between the studied materials (p < 0.001), with the highest mean ± SD reported in the milled IFDPs (174.42 ± 3.39, 27.13 ± 0.52), and the lowest in the conventional IFDPs (98.02 ± 6.1, 15.77 ± 0.32). Flexural strengths differed significantly between the conventional IFDPs and all materials except DLP AS. The highest elastic modulus was recorded in the milled group, and the lowest in the SLA ND group (p = 0.02). In conclusion, superior flexural strength, elastic modulus, and hardness were reported for milled IFDPs. SLA ND printed IFDPs showed comparable mechanical properties to milled ones except for the elastic modulus.