A Low-Temperature Phase Change Material Based on Capric-Stearic Acid/Expanded Graphite for Thermal Energy Storage

ACS Omega. 2021 Jul 2;6(28):17988-17998. doi: 10.1021/acsomega.1c01705. eCollection 2021 Jul 20.

Abstract

In this study, a capric acid (CA)-stearic acid (SA)/expanded graphite (EG) composite phase change material (PCM) was prepared, and the optimum mass ratio of CA-SA is 0.84:0.16. The composite PCM was characterized by scanning electron microscopy, differential scanning calorimetry, and X-ray diffraction. It can be concluded that the CA-SA mixture was found to possess good compatibility with EG, the thermal conductivity of the CA-SA/10 wt % EG composite PCM was 3.28 times higher than that of the CA-SA mixture, and the PCM thermal stability was satisfactory; no leakage occurred in the CA-SA/10 wt % EG composite PCM. The PCM has good thermal reliability after 500 thermal cycles. Finally, it is shown that the CA-SA/10 wt % EG composite PCM showed excellent performance, and therefore, it can be used for low-temperature thermal energy storage.