The objective of this study was to develop a simpler and more practical quantitative evaluation method of cold flow (CF) in transdermal drug delivery systems (TDDSs). CF was forcibly induced by loading a weight on a punched-out sample (bisoprolol and tulobuterol tapes). When the extent of CF was analyzed using the area of oozed adhesive as following a previously reported method, the CF profiles were looked different between the samples 12 mm in diameter subjected to a 0.5-kg weight and samples 24 mm in diameter subjected to a 2.0-kg weight despite an equal load per unit area (4.42 g/mm2). The width of oozed adhesive around the original sample was suggested to be an index that properly describes the relationship between the load per unit area and the extent of CF. Further, it was clarified that the average CF width over the entire circumference of the sample was the same whether the samples were round or square as long as the sample area and load were the same. We also observed a linear relationship between the CF width and the aspect ratio of oval and rectangular samples. These results indicated that the CF properties of typical TDDS products lacking CF-proof processing at the edges could be determined by testing samples cut from the product rather than the whole TDDS patch. The proposed width measuring method was simple and useful for optimizing the composition of the adhesive and for testing the quality of the product.
Keywords: bisoprolol; cold flow; transdermal drug delivery system; tulobuterol; width measuring method.