Light-induced, spatially well-defined, reversible switching of surface properties enables the creation of remote-controlled smart surfaces. We have taken advantage of the unique high-resolution structuring capabilities of extreme ultraviolet (EUV) interference lithography to produce nanostructured photoresponsive polymer brushes. Patterns of poly(glycidyl methacrylate) (PGMA) and poly(methacrylic acid) (PMAA) were grafted from two different 100 μm thick fluoropolymer substrates by means of a radiation-initiated, grafting-from approach based on free-radical polymerization (FRP). Photochromic properties were introduced via novel one- or two-step postpolymerization modifications with spiropyran (SP) derivatives, which allowed us to control the number of photochromic groups on the polymer brushes. Depending on the degree of functionalization and the local chemical environment, the SP moieties can open upon UV-light exposure to form zwitterionic, deeply colored, and fluorescent merocyanines (MCs) and reclose to the colorless SP configuration via thermal or visible light-induced relaxation. Switching kinetics were studied by means of time-resolved fluorescence microscopy and compared with kinetic measurements of the SP moiety in solution. The results indicated the importance, for the intensity of the switching, of the local chemical environment provided by both the polymer brush and added solvents, and showed the predominant influence on the ring-closing kinetics of polar solvents, which stabilize the MC form. To allow further characterization of the polymer-brush arrangements on a macroscopic scale, similar, but unstructured brush systems were grafted from fluoropolymers after large-area activation using EUV radiation or argon plasma. All steps of the postpolymerization modification were characterized in detail using attenuated total reflection infrared (ATR-IR) spectroscopy. Furthermore, a light-induced reversible static-contact-angle switch with a range of up to 15° for PGMA-SP brushes and up to 30° for PMA-SP brushes was demonstrated upon alternating UV- and visible-light irradiation.