High-temperature in-situ TEM straining of the interaction with dislocations and particles for Cu-added ferritic stainless steel

IntroductionCu is always present in the matrix when ferritic steels were prepared from ferrous scrap. When the ferritic steels are aged thermally, Cu precipitates start appear and disperse finely and homogeneously [1], which may make the steels strengthened by precipitation hardening. In this study, the interaction between Cu precipitates and dislocations was exmined via high-temperature in-situ TEM straining. ExperimentalCu-added ferritic stainless steel (Fe-18.4%Cr-1.5%Cu) was used in the present study. Specimen was aged at1073 K for 360 ks. Samples for TEM observation were prepared by focused ion beam (FIB; Quanta 3D 200i) method. Microstructure of specimen was analyzed by JEM-3200FSK and high-temperature in-situ TEM straining was conducted using JEM-1300NEF. Results and discussionInteraction between Cu precipitates and dislocation is seen from consecutive TEM images acquired by in-situ TEM straining at 1073 K, as shown in Fig.1. The size of Cu precipitates was about 70 nm and several dislocations were present within the field of view. In particular, progressing dislocations contacted with the Cu precipitate at right angle, as indicated by arrows in Fig.1 (b) to (d). This result implies that there is an attractive interaction between dislocations and the Cu precipitate. This is attributed to the fact that Stress field of dislocations was easily relaxed in interface between the Cu precipitate and matrix because of lattice and interface diffusion as well as slip in the interface [2,3]. Furthermore, dislocations pass through the particle after contacting it, so that the interaction with dislocations and particles should be explained by Srolovitz mechanism [4].jmicro;63/suppl_1/i28/DFU083F1F1DFU083F1Fig. 1.TEM images foucused on interaction with dislocations and partticles.