Guang Pu Xue Yu Guang Pu Fen Xi. 2013 Aug;33(8):2051-4.

[Effect of substrate temperature on structure and photoluminescence of ZnMgO films].

[Article in Chinese]

Author information

  • 1School of Physics and Electronic Technology, Liaoning Normal University, Dalian 116029, China. dlngaga@126.com

Abstract

ZnMgO films were deposited on quartz glass substrates by the ultrasonic spray pyrolysis at different substrate temperatures (450-550 degrees C). The structural, surface morphological and optical properties of the samples were investigated by X-ray diffraction (XRD), scanning electron microscope (SEM) and photoluminescence (PL) spectroscopy. The results demonstrate that the substrate temperature has important effect on structural and optical characteristics. All the films have hexagonal wurtzite polycrystalline structures and the c-axis preferential orientation has an optimum temperature of 530 degrees C. The sample prepared at this temperature owns uniform grain size, smooth surface morphology and better crystalline quality. The width of deep-level emission decreases and the near band edge (NBE) ultraviolet emission peak appears with the increase in temperature by the PL spectrum. When the temperature arrives to 530 degrees C, a distinct NBE emission peak can be observed at 374. 5 nm, while the deep level emission is almost undetectable.

PMID:
24159844
[PubMed]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Loading ...
    Write to the Help Desk