Octahedral tin dioxide nanocrystals as high capacity anode materials for Na-ion batteries.

Author information

  • 1Centre for Clean Energy Technology, School of Chemistry and Forensic Science, Faculty of Science, University of Technology, Sydney, Australia.

Abstract

Single crystalline SnO2 nanocrystals (~60 nm in size) with a uniform octahedral shape were synthesised using a hydrothermal method. Their phase and morphology were characterized by XRD and FESEM observation. TEM and HRTEM analyses identified that SnO2 octahedral nanocrystals grow along the [001] direction, consisting of dominantly exposed {221} high energy facets. When applied as anode materials for Na-ion batteries, SnO2 nanocrystals exhibited high reversible sodium storage capacity and excellent cyclability (432 mA h g(-1) after 100 cycles). In particular, SnO2 nanocrystals also demonstrated a good high rate performance. Ex situ TEM analysis revealed the reaction mechanism of SnO2 nanocrystals for reversible Na ion storage. It was found that Na ions first insert into SnO2 crystals at the high voltage plateau (from 3 V to ~0.8 V), and that the exposed (1 × 1) tunnel-structure could facilitate the initial insertion of Na ions. Subsequently, Na ions react with SnO2 to form NaxSn alloys and Na2O in the low voltage range (from ~0.8 V to 0.01 V). The superior cyclability of SnO2 nanocrystals could be mainly ascribed to the reversible Na-Sn alloying and de-alloying reactions. Furthermore, the reduced Na2O "matrix" may help retard the aggregation of tin nanocrystals, leading to an enhanced electrochemical performance.

PMID:
23793542
[PubMed]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Royal Society of Chemistry
    Loading ...
    Write to the Help Desk