Nanoscale Res Lett. 2013 Feb 15;8(1):80. doi: 10.1186/1556-276X-8-80.

Atomic layer deposition of high-density Pt nanodots on Al2O3 film using (MeCp)Pt(Me)3 and O2 precursors for nonvolatile memory applications.

Author information

  • 1State Key Laboratory of ASIC and System, School of Microelectronics, Fudan University, Shanghai, 200433, China. sjding@fudan.edu.cn.

Abstract

Pt nanodots have been grown on Al2O3 film via atomic layer deposition (ALD) using (MeCp)Pt(Me)3 and O2 precursors. Influence of the substrate temperature, pulse time of (MeCp)Pt(Me)3, and deposition cycles on ALD Pt has been studied comprehensively by scanning electron microscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy. Therefore, Pt nanodots with a high density of approximately 2 × 1012 cm-2 have been achieved under optimized conditions: 300°C substrate temperature, 1 s pulse time of (MeCp)Pt(Me)3, and 70 deposition cycles. Further, metal-oxide-semiconductor capacitors with Pt nanodots embedded in ALD Al2O3 dielectric have been fabricated and characterized electrically, indicating noticeable electron trapping capacity, efficient programmable and erasable characteristics, and good charge retention.

PMID:
23413837
[PubMed]
PMCID:
PMC3666895
Free PMC Article

Images from this publication.See all images (10)Free text

Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Icon for BioMed Central Icon for PubMed Central
    Loading ...
    Write to the Help Desk