Odontology. 2011 Jul;99(2):119-28. doi: 10.1007/s10266-011-0002-9. Epub 2011 Apr 23.

Effect of mucoprotein on the bond strength of resin composite to human dentin.

Author information

  • 1Department of Preventive and Restorative Dentistry, University of California, San Francisco, 707 Parnassus Avenue Room 3212, San Francisco, CA 94143-0758, USA. Lilliam.Pinzon@ucsf.edu

Abstract

The purpose of this study was to test the bond strength and analyze the morphology of the dentin-adhesive interface of two etch and rinse and two self-etch adhesive systems with two kinds of artificial saliva (with and without 450 mg/L mucin) contamination under different conditions of decontaminating the interface. Bonded specimens were sectioned perpendicularly to the bonded surface in 1-mm thick slabs. These 1-mm thick slabs were remounted in acrylic blocks and sectioned in sticks perpendicular to the bonding interfaces with a 1-mm(2) area. Nine specimens from each condition were tested after 24 h on a testing machine (Instron) at a speed of 0.5 mm/min for a total of 360 specimens. Mean and standard deviations of bond strength (MPa) were calculated. ANOVA showed significant differences as well as Fisher's PLSD intervals (p < 0.05). The following values are the results for different groups: Control group 34-60 MPa, saliva without mucin 0-52 MPa, and saliva with mucin 0-57 MPa. Failure sites were mixed and adhesive failure was common for the low bond strength results. P&BNT with ideal conditions and following the manufacturer's instructions (control) had the highest bond strengths and the dentin-adhesive interface exhibited an ideal morphology of etch-and-rinse system. SEM gave complementary visual evidence of the effect in the dentin/adhesive interface structure with some contaminated conditions compared with their respective control groups. This in vitro artificial saliva model with and without mucin showed that an organic component of saliva could increase or decrease the bond strength depending on the specific bonding agent and decontamination procedure.

PMID:
21516294
[PubMed - indexed for MEDLINE]
PMCID:
PMC3711545
Free PMC Article

Images from this publication.See all images (6)Free text

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Full text links

    Icon for Springer Icon for PubMed Central
    Loading ...
    Write to the Help Desk