Nat Nanotechnol. 2010 May;5(5):321-5. doi: 10.1038/nnano.2010.54. Epub 2010 Apr 4.

Facile synthesis of high-quality graphene nanoribbons.

Author information

  • 1Department of Chemistry and Laboratory for Advanced Materials, Stanford University, Stanford, California 94305, USA.

Erratum in

  • Nat Nanotechnol. 2011 Feb;6(2):132.

Abstract

Graphene nanoribbons have attracted attention because of their novel electronic and spin transport properties, and also because nanoribbons less than 10 nm wide have a bandgap that can be used to make field-effect transistors. However, producing nanoribbons of very high quality, or in high volumes, remains a challenge. Here, we show that pristine few-layer nanoribbons can be produced by unzipping mildly gas-phase oxidized multiwalled carbon nanotubes using mechanical sonication in an organic solvent. The nanoribbons are of very high quality, with smooth edges (as seen by high-resolution transmission electron microscopy), low ratios of disorder to graphitic Raman bands, and the highest electrical conductance and mobility reported so far (up to 5e(2)/h and 1,500 cm(2) V(-1) s(-1) for ribbons 10-20 nm in width). Furthermore, at low temperatures, the nanoribbons show phase-coherent transport and Fabry-Perot interference, suggesting minimal defects and edge roughness. The yield of nanoribbons is approximately 2% of the starting raw nanotube soot material, significantly higher than previous methods capable of producing high-quality narrow nanoribbons. The relatively high-yield synthesis of pristine graphene nanoribbons will make these materials easily accessible for a wide range of fundamental and practical applications.

PMID:
20364133
[PubMed]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Loading ...
    Write to the Help Desk