Electrochemical deposition of calcium phosphate (CAP) on valve metals such as Ta, Nb, and Zr, was performed by anodic oxidation with alternate polarity inversion at an applied 20 VDC. A saturated hydroxyapatite(HAP)-phosphoric acid solution (pH 3) was used as the electrolyte. FTIR, XRD, and XPS were employed to investigate the detailed characteristics of the deposition. HAP was precipitated on Ta; HAP including brushite and monetite on Nb; and HAP and monetite on Zr. The Ca/P atomic ratios were 1.3-1.5 by XPS, and HPO(4)(2- )bands were detected on Ta by FTIR. Therefore, the HAP precipitated on Ta was a Ca-deficient HAP. In addition, the XPS spectra of the specimens showed that phosphate ions were incorporated into the anodic oxide film. Deposits with nano-grain size were observed by AFM. The results confirmed that CAP with nano-grain size was deposited on valve metals by the anodic oxidation with polarity inversion.
Your browsing activity is empty.
Activity recording is turned off.
Turn recording back on