Langmuir. 2008 Sep 16;24(18):10340-4. doi: 10.1021/la801017h. Epub 2008 Aug 13.

Rapid development of hydrophilicity and protein adsorption resistance by polymer surfaces bearing phosphorylcholine and naphthalene groups.

Author information

  • 1Department of Materials Engineering, Department of Bioengineering, School of Engineering, Center for NanoBio Integration, The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo, Japan.

Abstract

In order to provide a protein adsorption resistant surface even when the surface was in contact with a protein solution under completely dry conditions, a new phospholipid copolymer, poly (2-methacryloyloxyethyl phosphorylcholine (MPC)- co-2-vinylnaphthalene (vN)) (PMvN), was synthesized. Poly(ethylene terephthalate) (PET) could be readily coated with PMvN by a solvent evaporation method. Dynamic contact angle measurements with water revealed that the surface was wetted very rapidly and had strong hydrophilic characteristics; moreover, molecular mobility at the surface was extremely low. When the surface came in contact with a plasma protein solution containing bovine serum albumin (BSA), the amounts of the plasma protein adsorbed on the dry surface coated with PMvN and that adsorbed on a dry surface coated with poly(MPC-co-n-butyl methacrylate) (PMB) were compared. Substantially lower protein adsorption was observed with PMvN coating. This is due to the rapid hydration behavior of PMvN. We concluded that PMvN can be used as a functional coating material for medical devices without any wetting pretreatment.

PMID:
18698868
[PubMed - indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Icon for American Chemical Society
    Loading ...
    Write to the Help Desk