Nano Lett. 2008 May;8(5):1461-71. doi: 10.1021/nl080453i. Epub 2008 Apr 5.

Localized surface plasmon resonances in aluminum nanodisks.

Author information

  • 1Department of Applied Physics, Chalmers University of Technology, 412 96 Göteborg, Sweden. christoph.langhammer@fy.chalmers.se

Abstract

The plasmonic properties of arrays of supported Al nanodisks, fabricated by hole-mask colloidal lithography (HCL), are analyzed for the disk diameter range 61-492 nm at a constant disk height of 20 nm. Strong and well-defined (UV-vis-NIR) localized surface plasmon resonances are found and experimentally characterized with respect to spectral peak positions, peak widths, total cross sections, and radiative and nonradiative decay channels. Theoretically, the plasmon excitations are described by electrostatic spheroid theory. Very good qualitative and quantitative agreement between model and experiment is found for all these observables by assuming a nanoparticle embedded in a few nanometer thick homogeneous (native) aluminum oxide shell. Other addressed aspects are: (i) the role of the strong interband transition in Al metal, located at 1.5 eV, for the plasmonic excitations of Al nanoparticles, (ii) the role of the native oxide layer, and (iii) the possibility of using the plasmon excitation as an ultrasensitive, remote, real-time probe for studies of oxidation/corrosion kinetics in metal nanoparticle systems.

PMID:
18393471
[PubMed - indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Icon for American Chemical Society
    Loading ...
    Write to the Help Desk