Effect of iron on acid demineralisation of bovine enamel blocks by a soft drink.

Author information

  • 1Social Dentistry Department, Bauru School of Dentistry, University of São Paulo, Bauru, Al. Octávio Pinheiro Brisolla, 9-75 Bauru, SP 17012-901, Brazil.

Abstract

OBJECTIVES:

The aim of this study was to evaluate, in vitro, the effect of iron on the acid demineralisation of bovine enamel blocks by a soft drink.

DESIGN:

Twenty-four blocks of bovine enamel were randomly assigned to two groups (experimental and control), which were exposed to 4 cycles of demineralisation in Coke containing or not 10 mmol/L of iron, respectively, and another 4 cycles of remineralisation in artificial saliva. The softening of enamel was evaluated by % superficial microhardness change (SMHC) and wear analysis. Data were analysed using t-test (p<0.05).

RESULTS:

With regard to %SMHC, the experimental group presented average values (+/-S.E.) of -85.3+/-0.9, that were significantly higher (t=4.7, p<0.01) than the ones observed for control group (-76.7+/-1.6). The experimental group presented a mean wear (+/-S.E.) of 2.3+/-0.2 microm, that was significantly lesser (t=3.7, p<0.01) than the one observed for the control group (3.5+/-0.2 microm).

CONCLUSIONS:

According to this protocol, iron at 10 mmol/L significantly reduced the wear, but significantly enhanced the %SMHC of enamel blocks submitted to erosion by Coke.

PMID:
17559795
[PubMed - indexed for MEDLINE]
PubMed Commons home

PubMed Commons

0 comments
How to join PubMed Commons

    Supplemental Content

    Icon for Elsevier Science
    Loading ...
    Write to the Help Desk