Solution-grown single-crystal Ge nanowires were used as conductive channels in field effect transistor devices to study the influence of surface states on their electron transport properties. Nanowires contacted with Pt electrodes using focused ion beam metal deposition exhibited linear current-voltage (IV) curves at room temperature with apparent resistivities ranging from 10(1) to 10(-1) Omega cm. In all cases, the nanowire conductance decreased with positive external electric fields applied perpendicular to the nanowire surface by a gate electrode, characteristic of p-type carrier accumulation at the nanowire surface. The field-induced change in conductance exhibited a time-dependent relaxation, with response time and magnitude of current decrease that depended on the nanowire surface chemistry. Nanowires treated with an organic passivation layer using a thermally initiated hydrogermylation reaction exhibited 2 orders of magnitude slower current relaxation and a smaller decrease in current relative to "bare" nanowires with oxidized surfaces.