Facile deposition of [60]fullerene and carbon nanotubes on ITO electrode by electrochemical oxidative polymerization of ethylenedioxythiophene.

Department of Chemistry and Biochemistry, Graduate School of Engineering, Kyushu University, Fukuoka 812-8581, Japan.

It was found that [60]fullerene encapsulated in p-sulfonatocalix[8]arene and single-walled carbon nanotubes (SWNTs) solubilized by sodium dodecylsulfate can be readily deposited on the ITO electrode by electrochemical oxidative polymerization of ethylenedioxythiophene (EDOT) without chemical modification of these carbon clusters. The driving force for the deposition is an electrostatic interaction between the anionic complexes and the cationic charges of poly(EDOT) formed in the oxidative polymerization process. The surface morphology was thoroughly characterized by scanning electron micrograph: the [60]fullerene/poly(EDOT) film is covered by nano-particles with 20-100 nm diameters whereas the SWNTs/poly(EDOT) film is covered by nanorods with several microm length and ca. 100 nm diameter. The results indicate that the anionic complexes act as nuclei for the polymer growth in the oxidation polymerization. Interestingly, when these modified ITO electrodes were photoirradiated, the appearance of a photocurrent wave was observed. The action spectra showed that the photoexcited energy of [60]fullerene or SWNTs is efficiently collected by the electroconductive poly(EDOT) film and transferred to the ITO electrode.

PMID: 12945707 [PubMed]