Previously, we reported the implantation of a single tissue engineered leaflet in the posterior position of the pulmonary valve in a lamb model. The major problems with this leaflet replacement were the scaffold's inherent stiffness, thickness, and nonpliability. We have now created a scaffold for a trileaflet heart valve using a thermoplastic polyester. In this experiment, we show the suitability of this material in the production of a biodegradable, biocompatible scaffold for tissue engineered heart valves. A heart valve scaffold was constructed from a thermoplastic elastomer. The elastomer belongs to a class of biodegradable, biocompatible polyesters known as polyhydroxyalkanoates (PHAs) and is produced by fermentation (Metabolix Inc., Cambridge, MA). It was modified by a salt leaching technique to create a porous, three-dimensional structure, suitable for tissue engineering. The trileaflet heart valve scaffold consisted of a cylindrical stent (1 mm X 15 mm X 20 mm I.D.) containing three valve leaflets. The leaflets were formed from a single piece of PHA (0.3 mm thick), and were attached to the outside of the stent by thermal processing techniques, which required no suturing. After fabrication, the heart valve construct was allowed to crystallize (4 degrees C for 24 h), and salt particles were leached into doubly distilled water over a period of 5 days to yield pore sizes ranging from 80 to 200 microns. Ten heart valve scaffolds were fabricated and seeded with vascular cells from an ovine carotid artery. After 4 days of incubation, the constructs were examined by scanning electron microscopy. The heart valve scaffold was tested in a pulsatile flow bioreactor and it was noted that the leaflets opened and closed. Cells attached to the polymer and formed a confluent layer after incubation. One advantage of this material is the ability to mold a complete trileaflet heart valve scaffold without the need for suturing leaflets to the conduit. Second advantage is the use of only one polymer material (PHA) as opposed to hybridized polymer scaffolds. Furthermore, the mechanical properties of PHA, such as elasticity and mechanical strength, exceed those of the previously utilized material. This experiment shows that PHAs can be used to fabricate a three-dimensional, biodegradable heart valve scaffold.