Preparation of bismuth nanowire encased in quartz template for Hall measurements using focused ion beam processing

Abstract

Forming electrodes on opposite sides of an individual bismuth nanowire was attempted to prepare for Hall measurements. Although a 1-mm-long bismuth nanowire which is completely covered with a quartz template has been successfully fabricated to prevent oxidation, it is very difficult to attach Hall electrodes on the opposite sides of the nanowire due to the quartz covering. One side of the cylindrical quartz template was removed by polishing without exposure of the nanowire to the atmosphere; the thickness between the polished template surface and the nanowire was estimated to be several micrometers. Focused ion beam processing was successfully employed to expose both surfaces of the nanowire under high vacuum by removing part of the quartz template. A carbon thin film was then deposited in situ on the wire surface to fabricate an electrical contact on the bismuth nanowire sample. Furthermore, the energy dispersive X-ray analysis was performed to the area processed by focused ion beam, and the bismuth component of the nanowire was successfully detected. It was confirmed that the focused ion beam processing was applicable to attach electrodes to bismuth nanowire for Hall measurement.

Keywords: Bismuth nanowire, Hall measurement, focused ion beam, thermoelectrics, 81.07.Gf

Background

Nanoscale structures such as superlattices and nanowires attract research interest due to their electrical transport properties. It has been expected that nanostructured thermoelectric materials would exhibit enhanced performance [1-5]. In particular, one-dimensional bismuth nanowires have been expected to show an enhanced figure of merit as thermoelectric materials [2,3]. Bismuth, as a semimetal, has interesting electrical properties such as small effective mass, low carrier density, and a long mean free path; and the properties of bismuth, such as its Fermi surface and effective mass, have been well studied [6,7]. Bismuth nanowires have been fabricated using several methods for the study of the thermoelectric properties of one-dimensional systems [8-13]. Our group has fabricated a bismuth microwire array using a glass template and individual nanowires using a quartz template by application of a liquid-phase high pressure injection method [14-24]. The quartz template possesses an individual hole of several-hundred-nanometer diameter and over 1 mm long and is fabricated by identical procedure of an optical fiber for us to make the nanowire [21]. The simultaneous measurement of the Seebeck coefficient and resistivity was successfully achieved using the bismuth nanowire. The results implied that the carrier mobility of a nanowire less than 1 μm in diameter was significantly reduced compared with that for a bulk bismuth sample due to the collision at the quartz template surface, which functioned as a boundary condition, as a result of the classical size effect [25,26]. Although we have considered variations in the mobility of each carrier in the nanowire sample using a mean free path limitation model, direct measurement results have not yet been reported. Discussions have been based only on the model and temperature dependence measurement results of Seebeck coefficient and resistivity. Therefore, the carrier density and mobility should be evaluated by Hall measurement.

Bismuth nanowires are usually fabricated by using alumina templates [8-11]. Since bismuth nanowires are covered with the alumina template, the template must be removed so that the electrodes can be attached at the opposite sides of the nanowire for Hall measurements. Even if the alumina template component was completely removed using acid, it has been reported that the bare surface of the bismuth nanowire is likely to be oxidized in the atmosphere. Therefore, removal of the oxide layer covering the nanowire surface is a very important process to achieve ohmic contact with the electrodes [27-29]. Recently, a new fabrication process for bismuth nanowires called on-film formation of nanowires was reported [30], where the oxidized surface was removed by ion beam sputtering, and electrodes were deposited in situ on the bismuth nanowire without breaking the vacuum. However, a majority of the bismuth nanowire area was oxidized.

In the current research, however, the bismuth nanowires were covered with a quartz template; therefore, oxidation of the wire surface is prevented. Although such nanowire has apparent advantages, it was not considered to be suitable for the four-wire and Hall measurements because it is very difficult to remove the quartz component locally. However, in the previous study, we had successfully fabricated electrodes on the surface of the bismuth nanowire with ohmic contact using polishing and focused ion beam (FIB) processing and performed four-wire resistance measurement [31]. A local area of the bismuth wire was successfully exposed, and a carbon electrode was deposited on the bismuth wire in situ. In this paper, this method was applied for the preparation of a Hall measurement sample and discussed for a nanowire covered with a quartz template. The quartz template was cut using FIB processing to successfully expose the opposite side surfaces of a bismuth nanowire under high vacuum, and a carbon electrode was then immediately deposited on the surface of the bismuth nanowire.

Methods

An individual bismuth nanowire sample covered with a quartz template was prepared for the experiment. The diameter and length of the nanowire were ca. 700 nm and >1 mm, respectively. The individual nanowire was located in the center of the quartz template, of which the diameter was ca. 0.5 mm. The nanowire could be observed through the template using an optical microscope, due to the transparency of the template. However, removal of the quartz component was a significant challenge, even though the nanowire could be identified within the template. Several methods was attempted to achieve the removal of the template, with the conclusion that the quartz component would be best removed using polishing and FIB processing. The process used to fabricate the electrical contact on the bismuth nanowire is summarized in Figure Figure1.1. Firstly, a side of the quartz template was removed by polishing, as shown in Figure Figure11 (a). The typical diameter of the template was over 0.5 mm, which made the polishing process relatively easy using an optical microscope. Polishing was continued to achieve a distance of ca. 1 μm between the template surface and the bismuth nanowire. The roughness of the polished side surface was less than ± 50 nm. A thin film Pt-Pd layer (ca. 10 nm) was deposited on the polished surface to prevent charge up during the FIB process. The layer was completely removed by FIB processing after the fabrication of the electrodes was completed. The bismuth nanowire sample was installed into a dual-beam FIB apparatus capable of scanning ion microscopy (SIM) and scanning electron microscopy (SEM). The typical vacuum used for FIB processing was approximately 4.0 × 10−5 Pa. During FIB processing, the position of the nanowire was not detected by SIM or SEM; however, the approximate position along the wire length was visualized using a position coordinate of the microscope. Gallium (Ga) ion beam sputtering was employed for FIB processing, with detection of the bismuth nanowire position, as shown in Figure Figure11 (b). The typical area of removed template was 3 × 10 μm, corresponding to the wire length direction and its perpendicular, respectively (Figure (Figure2a).2a). A very slow sputtering rate was used for careful identification of the wire from SIM imaging. The SIM imaging could not directly detect the bismuth nanowire signal unless the wire was exposed using FIB processing. However, the use of an accelerated Ga ion beam (30 kV) made it possible to detect where the nanowire was lying, even if the wire was not completely exposed, and this was recognized under low vacuum SEM with application of a high voltage. Unfortunately, the acceleration voltage and angle of the SEM detector in the dual-beam FIB apparatus were not suitable to identify the wire position when covered with quartz. The high voltage energy Ga ion beam could penetrate the low density quartz template and could be detected at the bismuth nanowire surface. Therefore, the density difference was detected by SIM imaging, as shown in Figure Figure2a.2a. The FIB processing was stopped right after the bismuth nanowire could be detected. The thickness between the surface of the template and the nanowire was estimated to be less than 500 nm. After successfully determining the position of the bismuth nanowire, rectangular portions of the template adjacent to the nanowire were removed by FIB to a depth of 5 μm from the quartz surface and a distance of 650 nm from the edge of bismuth nanowire (Figures (Figures11 (c) and 2b). The template with bismuth nanowire was then tilted (ca. 60º) to expose each wire side for FIB processing, as shown in Figure Figure11 (d). A small area of the quartz wall (typically 1 × 1 μm) was exposed to the Ga ion beam (Figure (Figure2c)2c) and was gradually eliminated under low current. The structure was not observed even if the nanowire was located in there because the nanowire was packed into the quartz template. The FIB was stopped when any structure was identified, as shown in Figures Figures11 (e) and 2c. Figure Figure33 shows an SEM image of the exposed side of the wire in the quartz template after completion of the FIB processing. The inset of Figure Figure33 shows a magnified image after FIB processing, which shows the diameter of the FIB hole was less than 100 nm. Therefore, there is a possibility to apply this technique to nanowires with diameters less than 100 nm. The detected position of the bismuth nanowire was consistent with that expected in Figure Figure2a2a and with the estimated distance between the template surface and nanowire. Therefore, we could conclude that this is a bismuth nanowire in the quartz template. Further processing was required at the opposite side (Figure (Figure2d)2d) to achieve a gap between both sides of the wire of typically <1 μm size, to enable taking Hall measurements with very small error. Inset of Figure Figure2d2d shows optical microscope image of the processed area. The nanowire could be observed through the quartz template. Thereby removal of the quartz component was successfully achieved using the FIB process without oxidation of the nanowire surface.

Figure 1
Schematic diagram showing the processing for preparation of a bismuth nanowire for Hall measurements. (a) Polishing, (b) detection of the nanowire location, (c) removal of the side parts of the template, (d) exposure of the wire surface, (e) 3-D view ...
Figure 2
SIM images during the FIB process. (a) Detection of the nanowire location, (b) removal of the side parts of the template, (c) side view tilted at 60º to expose the nanowire surface, and (d) top view of the processed area after FIB processing. ...
Figure 3
SEM image of the FIB processed area. The thick red line represents the location of the bismuth nanowire in the quartz template. The inset shows a magnified figure of the exposed side area of the nanowire. Points 1 and 2 indicate the locations used for ...

Results and discussion

It should be noted that there is a possibility that the bismuth component is vaporized when exposed to the Ga ion beam. Therefore, energy dispersive X-ray (EDX) analysis was performed at points 1 and 2 shown in Figure Figure3.3. Point 1 is the FIB-processed quartz template and is composed of Si and O as the main components of quartz, as shown in Figure Figure4.4. Although a Ga component was also observed due to the Ga ion beam processing, no bismuth component was detected at point 1. In contrast, at point 2 which was located in the center of the exposure area for the nanowire, the bismuth component was successfully detected (Figure (Figure4).4). The electron beam for EDX has a typical spread of 1 × 1 μm; therefore, Si and O components were also detected at point 2. Al was also detected as a component of the microscope stage. The difference between points 1 and 2 indicates that the bismuth component remained after FIB processing.

Figure 4
EDX spectra at points 1 and 2, as indicated in FigureFigure33.

Carbon electrodes were then deposited in situ on the exposed wire side surfaces to avoid oxidation and provide electrical contact points. Figure Figure55 shows a typical SEM image of carbon deposition on the exposed nanowire surface. The typical thickness of the carbon deposition was ca. 0.5 μm. After achieving the electrical contact, the carbon film layer was then extended to a copper electrode on the surface of the quartz template, as shown in Figure Figure11 (f) and (g). The expected length of carbon between the surface of the bismuth nanowire and copper electrode is approximately 20 μm; therefore, the resistance of the carbon component was estimated to be ca. 200 Ω at an assumed resistivity of 50 μΩ m. The resistance would be reduced for a thicker carbon film.

Figure 5
SEM image after carbon deposition onto the exposed side surface of the bismuth nanowire.

Figure Figure66 shows a schematic diagram of the configuration used for Hall measurements after polishing, FIB processing, and carbon deposition of the nanowire. The bismuth nanowire is fixed on an alumina plate as a back base prepared with copper electrodes. A thermometer is attached on the plate to measure the temperature. The thermocouple and heater are also attached in order to measure thermoelectromotive force for measurement of a Seebeck coefficient. The lead wires from the pad on the alumina plate are connected to the copper electrode located on the surface of the quartz template. The Hall effect signal in a magnetic field is measured using this configuration, which also makes it possible to perform resistance measurements by the four-probe method. The magnitude of the resistance using the two-probe method was relatively large due to the small diameter and long length of the nanowire. For example, the resistance of a bismuth nanowire with a diameter of 100 nm and a length of 1 mm was estimated to be ca. 166 kΩ for an assumed resistivity of 1.3 μΩm. The value is relatively large for the resistance measurements; therefore, the time constant of the circuit should be considered. If the four-probe method is used, then the resistance value can be easily controlled using a suitable gap for measurement of the voltage. Therefore, the configuration shown in Figure Figure66 enables the successful measurement of the electrical properties of nanowires, including not only the resistivity and Hall coefficient, but also the Seebeck and Nernst coefficients.

Figure 6
Schematic diagram showing the configuration used for Hall measurement of the bismuth nanowire.

The magnitudes of the Hall voltage measured for the nanowire are now discussed. The Hall coefficient (RH) for a two-carrier model is expressed by RH=rHepnb2p+nb2b=μnμp , where rH is the Hall factor, n and p are the electron and hole carrier densities, respectively, and b is the mobility ratio between electrons μn and holes μp[32]. The value of rH is almost 1, even if carrier scattering processes are assumed. The values of n and p are taken from [7] for that of bulk Bi. The b value was estimated to be from 3 to 10, depending on the crystal orientation [33], and a value of b = 3 was selected as a severe assumption. The Hall resistance RHall is approximately expressed as RHall=RHBlS=4RHBπd, where d and B are the wire diameter and the magnitude of the magnetic field, respectively. Here the cross section of the nanowire (S) and the gap between metal electrodes for the Hall measurement (l) are approximated by S=πd22 and l=d, respectively. Conditions of d = 100 to 1,000 nm were considered in B = 0.12 T, which satisfy the low magnetic field approximation at 300 K [34]. Therefore, the calculated |RHall| is estimated to be from 0.19 Ω at 1,000 nm to 1.9 Ω at 100 nm. The electric current introduced into the bismuth nanowire for the measurement should ideally be less than 1 μA due to the small heat capacity of the narrow wire and the high resistance, so that an increase in temperature and burn out can be avoided. The absolute value of the measured Hall voltage was estimated to be 190 nV to 1.9 μV under the same conditions. Nanovolt-order voltage can be measured using a lock-in amplifier with modulation of the introduced current and magnetic field, which confirms that the configuration (Figure (Figure6)6) enables the experimental measurement of the Hall coefficient. The Hall coefficient of the bismuth nanowire enables us to evaluate carrier density and mobility experimentally. Therefore, the temperature dependence of resistivity of bismuth nanowires less than 1 μm can be described by the measurement of carrier density and mobility more directly than the calculation model of our previous study. In ition, it will be possible to measure not only Hall coefficient but also Nernst coefficient using the configuration; then, various electrical properties of bismuth nanowires can be evaluated.

Conclusions

A method to attach Hall electrodes on opposite sides of an individual bismuth nanowire encased in a quartz template was demonstrated using polishing, FIB processing, and carbon deposition. An accelerated Ga ion beam was used to detect the position of the nanowire in the quartz template without exposure. The quartz component covering the nanowire was then successfully removed with the Ga ion beam to locally expose the opposite side surfaces of the nanowire. Carbon thin films were then deposited in situ on the exposed wire surfaces to form electrical contacts, while avoiding oxidation of the nanowire. EDX analysis of the processed area indicated that the bismuth component remained after FIB processing.

The mobility reduction of bismuth nanowires less than 1 μm in diameter due to mean free path limitation at wire boundary will be evaluated experimentally by Hall measurement. Moreover, further investigations are planned using the configuration to examine the temperature and wire diameter dependence of the thermoelectric properties of bismuth nanowires, and the influence of the quantum effect using much smaller diameter of bismuth nanowires will be also estimated.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

MM carried out experiments, the polishing, FIB processing, EDX analysis, and drafted the manuscript. YH and TK guided the idea and the experiments and revised the manuscript. TK participated in the design of the FIB processing. All authors read and approved final manuscript.

Authors' information

MM is a PhD candidate under associate professor YH in the department of engineering, Saitama University, Japan.

Acknowledgments

This research was supported in part by Grant-in-Aid for JSPS Fellows, Grant-in-Aid for Scientific Research (B) and (C), leading industrial technology development project grant funds of NEDO, Asahi Glass Foundation, Japan Aluminum Association, and TEPCO Memorial Foundation. This work was performed under the auspices of the National Institute for Fusion Science (NIFS) collaborative research (NIFS11KECA012) and NINS's Creating innovative research fields project (number NIFS08KEIN0091). This research was supported by the Nanotechnology network program (Center for Nanotechnology Network, National Institute for Material Science) of the Ministry of Education, Culture, Sports, Science and Technology.

References

  • Hicks LD, Dresselhaus MS. Effect of quantum-well structures on the thermoelectric figure of merit. Phys Rev B. 1993;47:12727–12731. doi: 10.1103/PhysRevB.47.12727. [PubMed] [Cross Ref]
  • Hicks LD, Dresselhaus MS. Thermoelectric figure of merit of a one-dimensional conductor. Phys Rev B. 1993;47:16631–16634. doi: 10.1103/PhysRevB.47.16631. [PubMed] [Cross Ref]
  • Dresselhaus MS, Lin YM, Rabin O, Jorio A, Souza Filho AG, Pimenta MA, Saito R, Samsonidze Ge G, Dresselhaus G. Nanowires and nanotubes. Mater Sci Eng C. 2003;23:129–140. doi: 10.1016/S0928-4931(02)00240-0. [Cross Ref]
  • Harman TC, Taylor PJ, Walsh MP, LaForge BE. Quantum dot superlattice thermoelectric materials and devices. Science. 2002;297:2229–2232. doi: 10.1126/science.1072886. [PubMed] [Cross Ref]
  • Venkatasubramanian R, Siivola E, Colpitts T, O'Quinn B. Thin-film thermoelectric devices with high room-temperature figures of merit. Nature. 2001;413:597–602. doi: 10.1038/35098012. [PubMed] [Cross Ref]
  • Dresselhaus MS. In: Conference on the Physics of Semimetals and Narrow Gap Semiconductors: 1970 March 20-21; Dallas. Carter DL, Bate RT, editor. New York: Pergamon Press; 1970. Electronic properties of the group V semimetals; pp. 3–33.
  • Michenaud J-P, Issi J-P. Electron and hole transport in bismuth. J Phys C: Solid State Phys. 1972;5:3061–3072. doi: 10.1088/0022-3719/5/21/011. [Cross Ref]
  • Heremans J, Thrush CM. Thermoelectric power of bismuth nanowires. Phys Rev B. 1999;59:12579–12583. doi: 10.1103/PhysRevB.59.12579. [Cross Ref]
  • Huber TE, Graf MJ. Electronic transport in a three-dimensional network of one-dimensional bismuth quantum wires. Phys Rev B. 1999;60:16880–16884. doi: 10.1103/PhysRevB.60.16880. [Cross Ref]
  • Liu K, Chien CL, Searson PC. Finite-size effects in bismuth nanowires. Phys Rev B. 1998;58:14681–14684. doi: 10.1103/PhysRevB.58.R14681. [Cross Ref]
  • Lin Y-M, Cronin SB, Ying JY, Dresselhaus MS, Heremans JP. Transport properties of Bi nanowire arrays. Appl Phys Lett. 2000;76:3944–3946. doi: 10.1063/1.126829. [Cross Ref]
  • Nikolaeva A, Huber TE, Gitsu D, Konopko L. Diameter-dependent thermopower of bismuth nanowires. Phys Rev B. 2008;77:035422.
  • Cornelius TW, Toimil-Molares ME, Neumann R, Karim S. Finite-size effects in the electrical transport properties of single bismuth nanowires. J Appl Phys. 2006;100:114307. doi: 10.1063/1.2388857. [Cross Ref]
  • Hasegawa Y, Ishikawa Y, Komine T, Huber TE, Suzuki A, Morita H, Shirai H. Magneto-Seebeck coefficient of a bismuth microwire array in a magnetic field. Appl Phys Lett. 2004;85:917–919. doi: 10.1063/1.1781390. [Cross Ref]
  • Hasegawa Y, Ishikawa Y, Morita H, Komine T, Shirai H, Nakamura H. Electronic transport properties of a bismuth microwire array in a magnetic field. J Appl Phys. 2005;97:083907. doi: 10.1063/1.1865342. [Cross Ref]
  • Hasegawa Y, Nakano H, Morita H, Kurokouchi A, Wada K, Komine T, Nakamura H. Aspect ratio dependence of magnetoresistivity in polycrystalline bismuth microwire arrays. J Appl Phys. 2007;101:033704. doi: 10.1063/1.2432876. [Cross Ref]
  • Hasegawa Y, Nakano H, Morita H, Komine T, Okumura H, Nakamura H. Power factor enhancement in a magnetic field using polycrystalline bismuth microwire arrays. J Appl Phys. 2007;102:073701. doi: 10.1063/1.2785003. [Cross Ref]
  • Iwasaki H, Morita H, Hasegawa Y. Evaluation of thermoelectric properties in Bi-microwires by the Harman method. Jpn J Appl Phys. 2008;47:3576–3580. doi: 10.1143/JJAP.47.3576. [Cross Ref]
  • Hasegawa Y, Ishikawa Y, Shirai H, Morita H, Kurokouchi A, Wada K, Komine T, Nakamura H. Reduction of contact resistance at terminations of bismuth wire arrays. Rev Sci Instrum. 2005;76:113902. doi: 10.1063/1.2126952. [Cross Ref]
  • Hasegawa Y, Murata M, Nakamura D, Komine T, Taguchi T, Nakamura S. Mobility estimation in microsized bismuth wire arrays. J Appl Phys. 2009;105:103715. doi: 10.1063/1.3133136. [Cross Ref]
  • Hasegawa Y, Murata M, Nakamura D, Komine T, Taguchi T, Nakamura S. Thermoelectric properties of bismuth micro/nanowire array elements pressured into a quartz template mold. J Electron Mater. 2009;38:944–949. doi: 10.1007/s11664-009-0781-8. [Cross Ref]
  • Hasegawa Y, Murata M, Nakamura D, Komine T. Reducing thermal conductivity of thermoelectric materials by using a narrow wire geometry. J Appl Phys. 2009;106:063703. doi: 10.1063/1.3212982. [Cross Ref]
  • Murata M, Nakamura D, Hasegawa Y, Komine T, Uematsu D, Nakamura S, Taguchi T. Electrical nanocontact between bismuth nanowire edges and electrodes. J Electron Mater. 2010;39:1536–1542. doi: 10.1007/s11664-010-1282-5. [Cross Ref]
  • Nakamura D, Murata M, Hasegawa Y, Komine T, Uematsu D, Nakamura S, Taguchi T. Thermoelectric properties of a 593-nm individual bismuth nanowire prepared using a quartz template. J Electron Mater. 2010;39:1960–1965. doi: 10.1007/s11664-009-1045-3. [Cross Ref]
  • Murata M, Nakamura D, Hasegawa Y, Komine T, Taguchi T, Nakamura S, Jovovic V, Heremans JP. Thermoelectric properties of bismuth nanowires in a quartz template. Appl Phys Lett. 2009;94:192104. doi: 10.1063/1.3133355. [Cross Ref]
  • Murata M, Nakamura D, Hasegawa Y, Komine T, Taguchi T, Nakamura S, Jaworski CM, Jovovic V, Heremans JP. Mean free path limitation of thermoelectric properties of bismuth nanowire. J Appl Phys. 2009;105:113706. doi: 10.1063/1.3131842. [Cross Ref]
  • Cronin SB, Lin Y-M, Rabin O, Black MR, Ying JY, Dresselhaus MS, Gai PL, Minet J-P, Issi J-P. Making electrical contacts to nanowires with a thick oxide coating. Nanotechnology. 2002;13:653–658. doi: 10.1088/0957-4484/13/5/322. [Cross Ref]
  • Vila L, Piraux L, George JM, Faini G. Multiprobe magnetoresistance measurements on isolated magnetic nanowires. Appl Phys Lett. 2002;80:3805–3807. doi: 10.1063/1.1478783. [Cross Ref]
  • Choi SH, Wang KL, Leung MS, Stupian GW, Presser N, Morgan BA, Robertson RE, Abraham M, King EE, Tueling MB, Chung SW, Heath JR, Cho SL, Ketterson JB. Fabrication of bismuth nanowires with a silver nanocrystal shadowmask. J Vac Sci Technol A. 2000;18:1326–1328. doi: 10.1116/1.582348. [Cross Ref]
  • Shim W, Ham J, Lee K, Jeung W, Johnson M, Lee W. On-film formation of Bi nanowires with extraordinary electron mobility. Nano Lett. 2009;9:18–22. doi: 10.1021/nl8016829. [PubMed] [Cross Ref]
  • Murata M, Yamamoto H, Tsunemi F, Hasegawa Y, Komine T. Four-wire resistance measurements of a bismuth nanowire encased in a quartz template utilizing focused ion beam processing. J Electron Mater. 2012;41:1442–1449. doi: 10.1007/s11664-012-1986-9. [Cross Ref]
  • Seeger K. Semiconductor Physics. 9. Berlin: Springer; 2004.
  • Gallo CF, Chandrasekher BS, Shutter PH. Transport properties of bismuth single crystals. J Apple Phys. 1963;34:144–152. doi: 10.1063/1.1729056. [Cross Ref]
  • Hasegawa Y, Ishikawa Y, Saso T, Shirai H, Morita H, Komine T, Nakamura H. A method for analysis of carrier density and mobility in polycrystalline bismuth. Physica B. 2006;382:140–146. doi: 10.1016/j.physb.2006.02.011. [Cross Ref]

Articles from Nanoscale Research Letters are provided here courtesy of Springer
PubReader format: click here to try

Formats:

Related citations in PubMed

See reviews...See all...

Cited by other articles in PMC

See all...

Links

  • PubMed
    PubMed
    PubMed citations for these articles

Recent Activity

Your browsing activity is empty.

Activity recording is turned off.

Turn recording back on

See more...