Nanoscale Res Lett. 2012; 7(1): 142.
Published online Feb 20, 2012. doi:  10.1186/1556-276X-7-142
PMCID: PMC3299585

Improvement in the photoelectrochemical responses of PCBM/TiO2 electrode by electron irradiation

Abstract

The photoelectrochemical (PEC) responses of electron-irradiated [6,6]-phenyl-C61-butyric acid methyl ester (PCBM)/TiO2 electrodes were evaluated in a PEC cell. By coating PCBM on TiO2 nanoparticle film, the light absorption of PCBM/TiO2 electrode has expanded to the visible light region and improved the PEC responses compared to bare TiO2 electrode. The PEC responses were further improved by irradiating an electron beam on PCBM/TiO2 electrodes. Compared to non-irradiated PCBM/TiO2 electrodes, electron irradiation increased the photocurrent density and the open-circuit potential of PEC cells by approximately 90% and approximately 36%, respectively at an optimum electron irradiation condition. The PEC responses are carefully evaluated correlating with the optical and electronic properties of electron-irradiated PCBM/TiO2 electrodes.

Keywords: photoelectrochemical cell, TiO2, electron irradiation, PCBM, band-edge tuning

Introduction

TiO2 has been widely used for photocatalysts because of its good chemical- and photostabilities to convert photon energy to electrical and chemical energies [1]. However, due to its wide bandgap, the light absorption is limited only to the ultraviolet (UV) region of the solar spectrum. Hence, sensitizing TiO2 with small bandgap semiconductors, such as quantum dots or organic dyes, has been extensively studied to harvest more photons in the visible light region of solar spectrum for the applications to quantum dot-sensitized solar cells [2-4], dye-sensitized solar cells [5-7], and photoelectrochemical (PEC) cells [8-10].

Along with this current research trends, combining TiO2 with carbonaceous nanomaterials has attracted much interest, and studies on these materials are increasing exponentially these days [11]. For instance, high performance photocatalysts such as carbon nanotube-TiO2 [12-14], fullerene-TiO2 (C60-TiO2) [15-17], and graphene-TiO2 [18,19] composites have been introduced by several groups and have shown enhanced photocatalytic activities. Notably, C60 has shown interesting effects when combined with TiO2: facilitating the separation of photo-generated charge carriers from TiO2 to C60 [15,16] or sensitizing TiO2 to absorb visible light [17]. However, the band-edge position of C60 is unfavorable for a sensitizer of TiO2 because the lowest unoccupied molecular orbital (LUMO) level of C60 is lower than the conduction band of TiO2 [17]. From the viewpoint of energy levels, [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) is a better candidate than C60 for the sensitization of TiO2. We expect that the photo-excited electrons of PCBM can be transferred to TiO2 more efficiently because the LUMO level of PCBM is slightly higher than the conduction band of TiO2 [20]. In our previous study, we have found that the band-edge positions as well as the bandgap of PCBM can be tuned by electron irradiation at different fluences [21]. We believe that electron irradiation technique can be an alternative and unique method to modify the molecular structure and tune the bandgap [22,23] compared to the conventional methods such as adjusting the particle size of quantum dots [24,25] or modifying the molecular structure of the dyes [26] for larger light absorption. In addition to the bandgap, the band-edge positions can also be tuned by electron irradiation compared to the conventional methods such as ionic adsorption for specific quantum dots [27] or by varying the conjugation linkers in organic dyes [28].

Based on our previous findings, we present here a novel approach to improve the PEC performance of PCBM/TiO2 electrodes using electron beam irradiation. The photocurrent density and open-circuit potential of PCBM/TiO2 were respectively improved by 90% and 36% by electron irradiation. The effects of the electron irradiation on the PEC performances of PCBM/TiO2 were systematically analyzed in this study.

Methods

Figure Figure11 shows the schematic representation of the preparation of PCBM/TiO2 electrode and subsequent electron irradiation. The as-received TiO2 nanoparticle paste (DSL 18NR-T, Dyesol Industries Pty Ltd., Queanbeyan, New South Wales, Australia) was deposited on a fluorine-doped tin oxide (FTO) glass substrate (8 Ωm-2, Dyesol) by a doctor blade technique. Before the deposition of TiO2 paste, FTO glass substrates were cut by 1.0 × 2.5 cm2 in dimension and were sonicated successively in acetone, isopropanol, ethanol, and deionized water for thorough cleaning and dried in N2 gas stream. After the deposition of TiO2 paste, subsequent annealing process was performed at 450°C for 30 min with a temperature increase rate of 1°C min-1. After the annealing, TiO2 nanoparticle film was formed. The as-prepared TiO2 electrodes were immersed vertically in a chlorobenzene solution containing 1.5 mM PCBM for 5 h while stirring. PCBM solution was prepared by dissolving PCBM (99.5% purity, Nano-C, Inc., Westwood, MA, USA) powder into chlorobenzene (≥99.5% purity, Sigma-Aldrich, St. Luois, MO, USA) solvent. After the immersion, the electrodes were washed in pure chlorobenzene several times and dried at ambient condition. As a result, PCBM/TiO2 electrodes, where a thin layer of PCBM was coated on the TiO2 nanoparticle electrodes, were prepared. Coating process of PCBM was carried out in darkness. The irradiation of an electron beam on PCBM/TiO2 electrodes was carried out at room temperature and in vacuum lower than 2 × 10-5 Torr. An electron beam was generated from a thermionic electron gun with electron energy of 50 keV, and current density of the electron beam was 1.6 μA cm-2. The electron fluence was varied by adjusting the irradiation time. PCBM/TiO2 electrodes were irradiated by 1, 2, and 4 h which correspond to electron fluence of 3.6 × 1016, 7.2 × 1016, and 1.44 × 1017 cm-2, respectively. Diffuse reflectance UV-visible (VIS) spectra of electron-irradiated PCBM/TiO2 powders were measured on a spectrometer (S-4100, SCINCO CO., LTD., Seoul, South Korea) by scratching the nanoparticle film off the FTO glass substrate.

Figure 1
Schematic representation of the preparation of PCBM/TiO2 electrode and subsequent electron irradiation. (A) Deposition of TiO2 paste by doctor blade technique. (B) Formation of TiO2 nanoparticle film by annealing the as-deposited TiO2 paste at 450°C ...

After electron irradiation of PCBM/TiO2 electrodes, a custom-made PEC cell was constructed to measure the PEC responses of electron-irradiated PCBM/TiO2 electrodes, which act as photo-anodes of PEC cells. The PEC cell has a three-electrode configuration comprising a photo-anode, a Pt wire as a cathode, and a saturated calomel electrode (SCE) (0.242 V vs. NHE, BAS Inc., West Lafayette, IN, USA) as a reference electrode. An aqueous solution of 1 M NaOH (Junsei Chemical Co., Ltd., Chuo-ku, Tokyo, Japan) was used as a supporting electrolyte after 30 min purging with N2 gas. The PEC response of the electrodes was recorded on a potentiostat (Model SP-50, BioLogic, Claix, France) by sweeping the potential from -1.2 to 0.5 V (vs. SCE) at a sweep rate of 100 mV s-1. The photo-anodes were illuminated with a solar simulator (Model LS-150, Abet Technologies, Inc., Milford, CT, USA) equipped with AM 1.5 filter. The illumination power was estimated as 80 mW cm-2 at the photo-anode surface by a digital photometer (ILT1400-A, International Light Technologies, Inc., Peabody, MA, USA).

Results and discussion

Figure Figure11 displays the schematic representation for the preparation of the PCBM/TiO2 photo-anodes of PEC cells. TiO2 nanoparticles (NPs) were firstly deposited to form a film on a FTO glass substrate. A uniform TiO2 NP film was formed by annealing the as-deposited TiO2 paste at 450°C for 30 min. The TiO2 NP film was submerged in a PCBM solution for 5 h, and consequently, the TiO2 NP film was coated with PCBM. Subsequently, the PCBM/TiO2 electrodes were irradiated with an electron beam. The energy of the electron beam was 50 keV, and the electron fluence was changed by controlling the irradiation time. These electron-irradiated PCBM/TiO2 films on FTO glass substrates were used as photo-anodes of PEC cells for water splitting. Figure Figure22 shows the field emission scanning electron microscopy (FESEM) images of the fabricated PCBM/TiO2 film. TiO2 NPs with the diameter of approximately 20 nm were deposited on a FTO glass substrate (see details in the 'Methods' section). As shown in the FESEM image, the TiO2 NPs were well interconnected with one another, forming a rigid film that is strongly attached to the FTO glass substrate. The thickness of the TiO2 NP film was approximately 16.5 μm.

Figure 2
FESEM images. (A) Top view and higher magnification (inset) and (B) cross-sectional view of TiO2 nanoparticle film.

We observed that transparent TiO2 NP film became slightly yellowish after the PCBM coating. The UV-VIS absorption spectra shown in Figure Figure33 more clearly characterize the optical properties of the TiO2 NP films. When PCBM was coated on TiO2, visible light absorption of TiO2 in the wavelength range of 390 to 800 nm was increased, while absorption of UV in the range of 300 to 360 nm was decreased. In addition, when PCBM/TiO2 was irradiated with an electron beam, the absorbance in both UV and visible light region decreased gradually as the electron fluence increased. In our previous work, we reported that the bandgap of electron-irradiated PCBM increased as the electron fluence was increased. The modification of the bandgap was attributed to the change in the molecular structure of PCBM by electron irradiation. From these facts, we could conclude that the effective bandgap of electron-irradiated PCBM/TiO2 also increased as the electron fluence increased (Figure (Figure44).

Figure 3
Diffuse reflectance UV-VIS spectra. (a) TiO2 and (b) PCBM/TiO2. PCBM/TiO2 irradiated at (c) 3.6 × 1016, (d) 7.2 × 1016, and (e) 1.44 × 1017 cm-2.
Figure 4
Band structure of PCBM after electron beam irradiation of different fluences. (a) Non-irradiated PCBM. (b) Irradiated PCBM at 3.6 × 1016, (c) 7.2 × 1016, and (d) 1.44 × 1017 cm-2.

In order to investigate the band-tuning effect caused by the electron irradiation, we tried to characterize the PEC cell device performances using the electron-irradiated PCBM/TiO2 electrodes. The measurement results of the PEC responses of bare TiO2, PCBM/TiO2, and electron-irradiated PCBM/TiO2 electrodes are listed on Table Table1,1, and the typical current density-potential curves of the electrodes are shown in Figure Figure5.5. The saturated current density at 0 V vs. saturated calomel electrode under dark conditions of all the electrodes was less than 15 μA cm-2. Under illumination of simulated solar light, bare TiO2 nanoparticle electrode shows saturated photocurrent density (Jph) of 176 μA cm-2 and open-circuit potential (Eocp) of -0.85 V vs. SCE. After coating PCBM on TiO2 nanoparticles, the PEC performance was improved: Jph and Eocp of PCBM/TiO2 electrode increased to 234 μA cm-2 and -1.05 V vs. SCE, respectively. The improvement in Jph and Eocp is attributed to the increment of visible light absorption of PCBM compared to that of TiO2. After electron irradiation of PCBM/TiO2 electrode at electron fluence of 3.6 × 1016 cm-2, Jph and Eocp increased from 234 to 306 μA cm-2 and -1.05 to -1.16 V vs. SCE, respectively. The PEC performance of PCBM/TiO2 electrode was further improved through electron irradiation of increased electron fluence. Both Jph and Eocp of electron-irradiated PCBM/TiO2 were increased with increasing the electron fluence. Jph increased to 333 μA cm-2, and Eocp increased to -1.16 V vs. SCE at the electron fluence of 7.2 × 1016 cm-2.

Table 1
Photoelectrochemical performance of various electrodes investigated
Figure 5
Current density-potential curves of TiO2 and PCBM/TiO2 electrodes irradiated at different electron fluences under illumination. (a) Non-irradiated TiO2 and (b) PCBM/TiO2. PCBM/TiO2 irradiated at (c) 3.6 × 1016, (d) 7.2 × 1016, and (e) ...

The fact that the PEC performance of PCBM/TiO2 electrode was improved by electron fluence is interesting because electron irradiation increases the bandgap of PCBM and accordingly decreases the light absorption. As verified in our previous work, the LUMO level of PCBM shifts upward to the vacuum energy level as electron fluence increases. Since the bandgap of PCBM is much lower than that of TiO2, electron-hole pairs produced in PCBM can contribute to the increase in the photo-current of TiO2. However, the energy difference between the LUMO energy level of PCBM and the conduction band edge minimum of pure TiO2 is 0.2 eV, which might not be high enough for efficient electron transfer from PCBM to TiO2 [29]. Since LUMO energy level of PCBM is up-shifted by electron irradiation, electron-irradiated PCBM provides higher driving force of electron injection from PCBM to TiO2 [25]. This can explain why Jph of electron-irradiated PCBM/TiO2 electrodes was increased by increasing the electron fluence. Moreover, the increase in the energy difference between the LUMO energy level of electron-irradiated PCBM and the conduction band edge minimum of TiO2 provides efficient charge separation of the photo-excited electron-hole pairs, thereby improving Eocp [30].

However, when the electron fluence was further increased to 1.44 × 1017 cm-2, the PEC performance of electron-irradiated PCBM/TiO2 became worse. As shown in Figure Figure4,4, the LUMO energy level of PCBM was constantly up-shifted toward the vacuum energy level as the electron fluence was increased. The up-shift in the LUMO energy level of electron-irradiated PCBM increases the driving force of electron injection from PCBM to TiO2. With the up-shift in the LUMO energy level, the bandgap of the electron-irradiated PCBM also increases with increasing the electron fluence. The increase in the bandgap reduces the light absorption of PCBM and consequently deteriorates the PEC performance. Therefore, electron irradiation induces the two contradictory effects on the PEC performance of the electron-irradiated PCBM/TiO2, and this suggests that there is an optimum electron fluence at which the PEC performance is maximized. In our experiments, Jph increased by approximately 90% and Eocp increased by approximately 36% compared to bare TiO2 at an optimum electron fluence at 7.2 × 1016 cm-2.

Conclusions

Using the fact that the electronic band structure of PCBM can be modified by electron irradiation, PCBM/TiO2 electrodes were fabricated and tested in a PEC cell. We observed that electron irradiation on PCBM/TiO2 electrodes led to an increase in Jph by approximately 90% and Eocp by approximately 36% at an optimum electron irradiation condition. These results show that electron irradiation approach can be a good tool to tune the bandgap and the band-edge positions of PCBM and provide an evidence that the approach is useful for PEC device application. We believe that the electron irradiation strategy can also control the electronic band structures of other organic semiconducting materials, and thus, this strategy can improve the performances of PEC and photocatalytic devices.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

The work was carried out by the collaboration between all authors. SOC initiated the idea of electron irradiation on PCBM/TiO2 electrodes. SHY performed the electron irradiation experiments. SHY and GA performed the construction of PEC cell and measurement of PEC responses of electron-irradiated PCBM/TiO2 electrodes. JMK and SHH carried out the diffuse reflectance UV-VIS spectroscopy measurements of electron-irradiated PCBM/TiO2. SOC and SHY analyzed the data and suggested the mechanism of improvement of electron-irradiated PCBM/TiO2 electrodes. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by the National Research Foundation of Korea (NRF) grant funded by the Korean government (MEST) (no. 2011-0020764).

References

  • Hoffmann MR, Martin ST, Choi W, Bahnemann DW. Environmental applications of semiconductor photocatalysis. Chem Rev. 1995;95:69. doi: 10.1021/cr00033a004. [Cross Ref]
  • Lee YL, Huang BM, Chien HT. Highly efficient CdSe-sensitized TiO2 photoelectrode for quantum-dot-sensitized solar cell applications. Chem Mater. 2009;20:6903.
  • Xie Y, Ali G, Yoo SH, Cho SO. Sonication-assisted synthesis of CdS quantum-dot-sensitized TiO2 nanotube arrays with enhanced photoelectrochemical and photocatalytic activity. ACS Appl Mater Interfaces. 2010;2:2910. doi: 10.1021/am100605a. [PubMed] [Cross Ref]
  • Chen C, Ali G, Yoo SH, Kum JM, Cho SO. Improved conversion efficiency of CdS quantum dot-sensitized TiO2 nanotube-arrays using CuInS2 as a co-sensitizer and an energy barrier layer. J Mater Chem. 2011;21:16430. doi: 10.1039/c1jm13616j. [Cross Ref]
  • O'regan B, Grätzel M. A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films. Nature. 1991;353:737. doi: 10.1038/353737a0. [Cross Ref]
  • Bach J, Lupo D, Comte P, Moser JE, Weissörtel F, Salbeck J, Spreitzer H, Grätzel M. Solid-state dye-sensitized mesoporous TiO2 solar cells with high photon-to-electron conversion efficiencies. Nature. 1998;395:583. doi: 10.1038/26936. [Cross Ref]
  • Law M, Greene LE, Johnson JC, Saykally R, Yang P. Nanowire dye-sensitized solar cells. Nature Mater. 2005;4:455. doi: 10.1038/nmat1387. [PubMed] [Cross Ref]
  • Hodes G. A thin-film polycrystalline photoelectrochemical cell with 8% solar conversion efficiency. Nature. 1980;285:29. doi: 10.1038/285029a0. [Cross Ref]
  • Heller A. Conversion of sunlight into electrical power and photoassisted electrolysis of water in photoelectrochemical cells. Acc Chem Res. 1981;14:154. doi: 10.1021/ar00065a004. [Cross Ref]
  • Grätzel M. Photoelectrochemical cells. Nature. 2001;414:338. doi: 10.1038/35104607. [PubMed] [Cross Ref]
  • Leary R, Westwood A. Carbonaceous nanomaterials for the enhancement of TiO2 photocatalysis. Carbon. 2011;49:741. doi: 10.1016/j.carbon.2010.10.010. [Cross Ref]
  • Yao Y, Li G, Ciston S, Lueptow RM, Gray KA. Photoreactive TiO2/carbon nanotube composites: synthesis and reactivity. Environ Sci Technol. 2008;42:4952. doi: 10.1021/es800191n. [PubMed] [Cross Ref]
  • Gao B, Peng C, Chen GZ, Li Puma G. Photo-electro-catalysis enhancement on carbon nanotubes/titanium dioxide (CNTs/TiO2) composite prepared by a novel surfactant wrapping sol-gel method. Appl Catal B. 2008;85:17. doi: 10.1016/j.apcatb.2008.06.027. [Cross Ref]
  • Xia XH, Jia ZJ, Yu Y, Liang Y, Wang Z, Ma LL. Preparation of multi-walled carbon nanotube supported TiO2 and its photocatalytic activity in the reduction of CO2 with H2O. Carbon. 2007;45:717. doi: 10.1016/j.carbon.2006.11.028. [Cross Ref]
  • Krishna V, Noguchi N, Koopman B, Moudgil B. Enhancement of titanium dioxide photocatalysis by water-soluble fullerenes. J Colloid Interface Sci. 2006;304:166. doi: 10.1016/j.jcis.2006.08.041. [PubMed] [Cross Ref]
  • Long Y, Lu Y, Huang Y, Peng Y, Lu Y, Kang SZ, Mu J. Effect of C60 on the photocatalytic activity of TiO2 nanorods. J Phys Chem C. 2009;113:13899. doi: 10.1021/jp902417j. [Cross Ref]
  • Meng ZD, Zhu L, Choi JG, Chen ML, Oh WC. Effect of Pt treated fullerene/TiO2 on the photocatalytic degradation of MO under visible light. J Mater Chem. 2011;21:7596. doi: 10.1039/c1jm10301f. [Cross Ref]
  • Zhang H, Lv X, Li Y, Wang Y, Li J. P25-graphene composite as a high performance photocatalyst. ACS Nano. 2010;4:380. doi: 10.1021/nn901221k. [PubMed] [Cross Ref]
  • Zhou K, Zhu Y, Yang X, Jiang X, Li C. Preparation of graphene-TiO2 composites with enhanced photocatalytic activity. New J Chem. 2011;35:353. doi: 10.1039/c0nj00623h. [Cross Ref]
  • Kamat PV, Haria M, Hotchandani S. C60 cluster as an electron shuttle in a Ru(II)-polypyridyl sensitizer-based photochemical solar cell. J Phys Chem B. 2004;108:5166. doi: 10.1021/jp0496699. [Cross Ref]
  • Yoo SH, Kum JM, Cho SO. Tuning the electronic band structure of PCBM by electron irradiation. Nanoscale Research Letters. 2011;6:545. doi: 10.1186/1556-276X-6-545. [PMC free article] [PubMed] [Cross Ref]
  • Lee HM, Kim YN, Kim BH, Kim SO, Cho SO. Fabrication of luminescent nanoarchitectures by electron irradiation of polystyrene. Adv Mater. 2005;17:120. doi: 10.1002/adma.200400376. [Cross Ref]
  • Li Y, Lee EJ, Cai W, Kim KY, Cho SO. Unconventional method for morphology-controlled carbonaceous nanoarrays based on electron irradiation of polystyrene colloidal monolayer. ACS Nano. 2008;2:1108. doi: 10.1021/nn8001483. [PubMed] [Cross Ref]
  • Kongkanand A, Tvrdy K, Takechi K, Kuno M, Kamat PV. Quantum dot solar cells. Tuning photoresponse through size and shape control of CdSe-TiO2 architecture. J Phys Chem C. 2008;112:18737. [PubMed]
  • Kamat PV. Quantum dot solar cells. Semiconductor nanocrystals as light harvesters. J Phys Chem C. 2008;112:18737.
  • Robertson N. Optimizing dyes for dye-sensitized solar cells. Angew Chem Int Ed. 2006;45:2338. doi: 10.1002/anie.200503083. [PubMed] [Cross Ref]
  • Peter LM, Wijayantha KGU, Riley DJ, Waggett JP. Band-edge tuning in self-assembled layers of Bi2S3 nanoparticles used to photosensitize nanocrystalline TiO2. J Phys Chem B. 2003;107:8378. doi: 10.1021/jp030334l. [Cross Ref]
  • Hagberg DP, Marinado T, Karlsson KM, Nonomura K, Qin P, Boschloo G, Brinck T, Hagfeldt A, Sun L. Tuning the HOMO and LUMO energy levels of organic chromophores for dye sensitized solar cells. J Org Chem. 2007;72:9550. doi: 10.1021/jo701592x. [PubMed] [Cross Ref]
  • Wang ZS, Yamaguchi T, Sugihara H, Arakawa H. Significant efficiency improvement of the black dye-sensitized solar cell through protonation of TiO2 films. Langmuir. 2005;21:4272. doi: 10.1021/la050134w. [PubMed] [Cross Ref]
  • Lin CJ, Lu YT, Hsieh CH, Chien SH. Surface modification of highly ordered TiO2 nanotube arrays for efficient photoelectrocatalytic water splitting. Appl Phys Lett. 2009;94:113102. doi: 10.1063/1.3099338. [Cross Ref]

Articles from Nanoscale Research Letters are provided here courtesy of Springer
PubReader format: click here to try

Formats:

Related citations in PubMed

See reviews...See all...

Cited by other articles in PMC

See all...

Links

Recent Activity

Your browsing activity is empty.

Activity recording is turned off.

Turn recording back on

See more...