Two novel hierarchical homogeneous nanoarchitectures of TiO2 nanorods branched and P25-coated TiO2 nanotube arrays and their photocurrent performances

Abstract

We report here for the first time the synthesis of two novel hierarchical homogeneous nanoarchitectures of TiO2 nanorods branched TiO2 nanotube arrays (BTs) and P25-coated TiO2 nanotube arrays (PCTs) using two-step method including electrochemical anodization and hydrothermal modification process. Then the photocurrent densities versus applied potentials of BTs, PCTs, and pure TiO2 nanotube arrays (TNTAs) were investigated as well. Interestingly, at -0.11 V and under the same illumination condition, the photocurrent densities of BTs and PCTs show more than 1.5 and 1 times higher than that of pure TNTAs, respectively, which can be mainly attributed to significant improvement of the light-absorbing and charge-harvesting efficiency resulting from both larger and rougher surface areas of BTs and PCTs. Furthermore, these dramatic improvements suggest that BTs and PCTs will achieve better photoelectric conversion efficiency and become the promising candidates for applications in DSSCs, sensors, and photocatalysis.

Introduction

In current years, one-dimensional (1D) TiO2 nanostructure materials, especially nanotubular [1-3] and hierarchical [4-7] nanoarchitecture TiO2 nanotube arrays (TNTAs), have initiated increasing research interest owing to their intriguing architectures because they possess very high specific surface areas and a dual-channel for the benefit of the electrons transportation from interfaces to electrodes [7-13]. These nanostructure materials have shown very promising applications in dye-sensitized solar cells (DSSCs) [14-16], photocatalysis [17-19], photosplitting water [20,21], sensors [22,23], photoelectrochemical cells [24], and piezoelectronics [25]. However, as far as we are concerned, tremendous efforts have been conducted to improve the geometrical factors of the nanotube layers [8-13,26], to convert amorphous TiO2 nanotubes into different crystalline forms (i.e., anatase or rutile phase, or mixture phases of anatase and rutile) through high temperature annealing for high performance applications [27-29], and also many studies have devoted one's mind to change the crystal structure or chemistry composition of the tubes by modifying and doping [30-33]. There still remain many challenges to prepare and discuss the homogeneous modification of TNTAs, although the similar synthesis method of growing branched ZnO nanowires [34] and the decoration process of growing TiO2 nanoparticles on TiO2 nanotubes by a TiCl4 treatment [35] have been reported. Therefore, it is particularly valuable to seek some facile and high-efficiency method to synthesize the modification of TNTAs nanostructures for further specific surface area.

In this communication, we report for the first time the synthesis of two novel hierarchical homogeneous modification nanoarchitectures (i.e., P25-coated TNTAs, PCTs; and TiO2 nanorods branched TNTAs, BTs) via two-step method of electrochemical anodization and hydrothermal modification approach. The main precursors of modification are the P25 (Degussa, Germany) and titanium(IV) isopropoxide (TTIP of 95%). Erenow, the optimized nanoarchitecture TNTAs (with bigger pore diameter, longer length, and larger space among tubes) have been prepared by electrochemical anodization method. Interestingly, the as-synthesized BTs and PCTs with beautiful morphologies show both larger and rougher surface area, and these properties result in dramatic improvement of light-absorbing and charge-harvesting efficiency, which has been shown through the UV-Vis diffuse reflectance spectroscopic spectra and photoelectrochemical performances in this article.

Experimental section

Fabrication of optimum nanoarchitecture TNTAs

In this article, TNTAs were prepared using a typical anodization approach [13]. Briefly, the fabrication process of the optimum nanoarchitecture TNTAs with bigger pore diameter, larger space among tubes and longer length was described as follows, Titanium foil samples, about 200 μm × 2 cm × 3.5 cm (Purity≥99.6%, from ShengXin non-ferrous metal Co., LTD, Baoji, Shanxi, China) were cleaned with soap, acetone, and iso-propanol before anodization. A two-electrode configuration was used for anodization, with Ti foil as the anode, and platinum foil as the cathode. A 99.7% pure Ti foil (0.2 mm thickness, 2 × 3 cm2) was immersed in the electrolyte containing 0.35 wt% NH4F (85% Lactic Acid) and 10 vol.% DMSO (dimethyl sulphoxide: purity ≥99.0%) at a 45 V constant potential for 9 h. Thus we obtained the amorphous TNTAs, and then the as-prepared TNTAs were annealed at 400°C for 1.5 h for further use.

Synthesis of hierarchical homogeneous nanoarchitecture BTs

The BTs were obtained via a modification process of growing TiO2 nanorods on the as-prepared TNTAs by conventional hydrothermal growth method. Briefly, the as-prepared TNTAs were immersed in a beaker with growth solution, this solution was consisted of 90 mL of 0.8 M HCl (36-38%) with constant stirring at 25°C for about 15 min. After that, 6 mL of TTIP of 95% as precursor was dropped (0.16 μL/s) in mixture solution, kept stirring for 1 h [7,32,33], and then the beaker was sealed and heated at 95°C for 9 h, with slight stirring maintained for the entire heating process to grow TiO2 nanorods on the TNTAs. After the reaction, the reactant was cooled freely to room temperature and washed several times with ethanol and distilled water, and the as-prepared BTs were obtained. The BTs were finally achieved through annealing in a muffle furnace at 400°C for 2 h.

Fabrication of hierarchical homogeneous nanoarchitecture PCTs

We fabricated PCTs via a hydrothermal approach of coating P25 on the as-prepared TNTAs. About 0.4 g P25 (Degussa, Germany) was put into a beaker with 300 mL of distilled water, then they were mixed through vigorous magnetic stirring and ultrasonicating alternately at room temperature more than 5 times (about 10 min per time), After that, the mixed solution was kept state static more than 3 h, and then transferred into a Teflon-lined autoclave (80 mL), in which the as-prepared TNTAs were suspended. The autoclave was sealed and heated at 80-120°C for 12 h to coat P25 on the TNTAs, and then it was cooled freely to room temperature and washed several times with distilled water, thus the as-prepared PCTs were obtained. Finally, the PCTs were fabricated after the as-prepared PCTs were annealed at 400°C for 2 h.

Characterization

The crystal structures of the as-synthesized samples were firstly determined by using a Bruker D8 advance X-ray diffractometer (XRD, Cu Kα radiation; λ = 1.5418 Å). Then the morphologies were observed by field-emission scanning electron microscopy (FESEM, JOEL, JSM-6700F), and transmission electron microscopy (TEM and HRTEM, JEM-2010FEF; 200 kV). Photoelectrochemical experiments were carried out using a three-electrode configuration (CH instruments, CHI 660C) with a Pt wire counter electrode, a reference saturated calomel electrode and a working electrode. The all samples used as working electrodes were illuminated with a 150~350 W adjustable xenon lamp (from Shanghai Lansheng Electronics Co., LTD., Model, XQ350W). The measured light irradiance was approximately 100 mW/cm2, and the scan rate was 100 mV/s

Results and discussion

In this study, the two-step method is used to synthesize the BTs and PCTs. The first step is the fabrication of the optimize nanoarchitecture TNTAs [36,37]. From Figure Figure1,1, it can be found that the TNTAs show very nice highly ordered, self-organized, and free-standing morphologies, and the optimize geometrical architectures (average external diameter, 350 nm; tube length, 3.5 μm; wall thickness, 10 nm; and space among tubes, 60 nm), and also show at least local single-crystalline status. These characterizations can be observed from the FESEM images of the top view and cross-section of the TNTAs shown in Figure Figure1a1a and the TEM, SAED, and HRTEM images in Figure Figure1b1b.

Figure 1
Characterization images of the TNTAs see (a) and (b): (a) Low-magnification FESEM, insets are enlarged FESEM images of the top view and cross-section of its typical tubes, respectively; (b). TEM image of the individual TiO2 nanotube, insets are its HRTEM ...

The second step is the synthesis of BTs and PCTs using hydrothermal modification method. In brief, they were obtained from growing branched TiO2 nanorods and coating P25 on the pre-prepared TNTAs via hydrothermal modification process, the images of obtained BTs and PCTs are shown in Figures Figures22 and and3,3, respectively. As for the BTs, the mechanism of the formation of TiO2 crystal nucleus and growth of the anisotropic 1D nanocrystalline TiO2 nanorods, and their corresponding FESEM images are depicted in Figure Figure4.4. From schematic diagram of the morphologies evolution of the BTs and the FESEM images, it is clearly observed that more and more TiO2 nanocrystal nucleus were firstly formed on the rough surfaces of the TiO2 tubes with special bamboo structures, many rings and attached particles, these special structures and morphologies are the probable cause of crystal nucleus formed. And then the nucleus gradually grew up and became increasing TiO2 nanorods along the backbones of the TiO2 tubes, along with a small quantity of free-grown rods random adhered to the backbones of the tubes. Thus these TiO2 nanorods made BTs have both larger and rougher surface area [7,34]. Furthermore, the same conclusion can also be confirmed by the top view FESEM images showed in Figure 2a, c, the cross-sectional view in Figure Figure2b,2b, the TEM image of a individual branched TiO2 nanotube in Figure Figure2d.2d. And the insets in Figure Figure2d2d are the SAED pattern and the HRTEM images, which show the BTs are evident polycrystalline.

Figure 2
FESEM images of (a) top view, (b) cross-section view, (c) high-magnification top view of BTs. (d) TEM image of a typical individual branched TiO2 nanotube shown in (a); insets are its SAED and HRTEM images of the marked areas, respectively.
Figure 3
FESEM images of (a) top view, (b) cross-section view, (c) high-magnification top view of PCTs. (d) TEM image of several typical PCTs shown in (a); insets are their SAED and HRTEM images of the marked areas, respectively.
Figure 4
The section on the left is the morphology evolution of BTs, and their corresponding FESEM images are on the right.

Figure Figure33 is the characterization of another homogeneity nanostructure (the PCTs). Figure Figure3a3a is the top view FESEM image of the PCTs. A cross-sectional view in Figure Figure3b3b shows that the length of the tubes is the same as that of TNTAs (about 3.5 μm) and the P25 nanoparticles are densely grown on the whole surface (including inside and outside) of the TiO2 tubes. And the top view of the PCTs with many attached P25 particles is clearly shown by the high-magnification FESEM image in Figure Figure3c.3c. Meanwhile, Figure Figure3d3d shows the PCTs' TEM image, and its inset of the HRTEM image shows the (101) crystal facet and the 0.35 nm interplane distance of a typical anatase TiO2 while the another inset of the SAED pattern shows that the PCTs are polycrystalline structure [24]. The growth mechanism of the PCTs is mainly dependent on the special structures and morphology of TNTAs, especially its bigger pore diameter, larger space among tubes, and rough surface. Moreover, annealing plays an important role in the process of transforming the P25 on the TiO2 tube surface from attached state into crystallization state.

Otherwise, the X-ray diffraction (XRD) patterns in Figure 5a, b, c are also employed to characterize the properties of the obtained samples. We can find that the diffraction peaks of the samples (b, c) and the dominant diffraction peaks of the samples (a) match well with the crystal structure of the anatase TiO2 phase (JCPDS 21-1272) [38] except for one peak of the Ti (101). The main reason can be attributed to thermal treatment temperature of no more than 400°C for 2 h. It is noteworthy that the two peaks [R (110) and R (211)] in Figure Figure5a5a just match with the crystal structure of the rutile TiO2 nanorod (JCPDS no. 21-1276) [7,12], this comes from those rutile TiO2 nanorods grown on the TNTAs.

Figure 5
XRD patterns of (a) BTs, (b) PCTs, and (c) TNTAs.

On the basis of the above observations and structural analyses, we conclude that both of the BTs and PCTs can provide larger and rougher surface areas than the TNTAs compared with the arrays of same geometrical size and quantity [7,34,35]. As a result, this larger and rougher surface areas are favorable to improve light-absorbing and charge-harvesting efficiency and to absorb more dye for better photoelectric conversion efficiency and better applications such as photocatalysis, sensors, etc. Moreover, it is also found that the growth length and density of the TiO2 nanorods of the BTs can be readily controlled by adjusting the growth time and the concentration of growth solution, and that the density of the coated P25 particles can also be controlled through changing the coating time and the concentration of coating solution.

Figure Figure66 shows the UV-Vis diffuse reflectance spectra of three samples (TNTAs, PCTs, and BTs) and Ti foil. Comparing to the UV-Vis absorption spectrum of the TNTAs, the absorption edges of the samples (PCTs and BTs) displayed appreciable shifts (BTs is a little bit larger than PCTs) to visible region revealing some decreases in their band gaps. This conclusion is mainly consistent with the above discussions and the previous studies [39-41]. Simultaneously, it can also be found that the absorption intensity of each sample (TNTAs, PCTs, and BTs) is gradually increasing after their absorption peaks. The cause for this effect mainly comes from absorption effect of the annealed (400°C, 2 h) Ti foil substrate to visible (see the inset in Figure Figure6).6). Otherwise, the general UV-Vis absorption spectra only reflect the intrinsic optical property for the bulk of a solid. However, the actual absorption spectrum of a photocatalyst is an overlapping result of intrinsic and extrinsic absorption bands [42].

Figure 6
UV-Vis diffuse reflectance spectra of the samples (TNTAs, PCTs, BTs, and inset, Ti foil).

Furthermore, Figure Figure77 clearly shows the comparison curves of the photocurrent densities versus applied potentials for three different TiO2 photoanodes (TNTAs, BTs, and PCTs) under Xe lamp irradiation (100 mW/cm2) in 1 M KOH electrolyte [43]. It can be observed that the values of the photocurrent densities of BTs and PCTs are dramatically greater than that of TNTAs. At -0.11 V and under the same illumination conditions, the photocurrent density of BTs shows more than 1.5 times higher than that of TNTAs while PCTs versus TNTAs is more than 1 times higher. These experimental results are well consistent with the effect from above UV-Vis diffuse reflectance spectra. They suggest that the BTs and PCTs used as photoanodes can harvest more solar light and more photogenerated charge than that of the TNTAs with the same geometrical structure. In addition, the photocurrent densities of the BTs and PCTs also show a steeper increase when their applied potentials are over -0.7 V. Thus as for the BTs and PCTs, e--h+ pairs induced by photon absorption are split more readily compared with the TNTAs. The conclusion mainly results from the fact that more incident photons are absorbed on the electrode with larger and rougher space area [44].

Figure 7
Variation curves of photocurrent densities versus measured potentials for three different photoanodes (TNTAs, PCTs, and BTs) in 1 M KOH electrolyte.

Conclusion

In summary, we have reported here the fabrication of two novel hierarchical homogeneous nanoarchitectures of BTs and PCTs with larger and rougher surface areas via facile hydrothermal modification process. Based on the investigation of the photocurrent densities versus applied potential, the photocurrent density of BTs, at -0.11 V and under the same illumination conditions, shows more than 1.5 times higher than that of TNTAs while PCTs versus TNTAs is more than 1 times higher. On the basis of the results and discussion, we conclude that the dramatically improved photocurrent densities of the BTs and PCTs used as photoanodes are mainly due to their better incident photons and photogenerated charge-harvesting capability compared to TNTAs resulting from their further enhanced and rough surface areas. As a result, our study will also provide a new approach in conformating hierarchical homogeneity nanostructure materials and presenting two kinds of promising candidates for applications in DSSCs, sensors, and photocatalysis.

Abbreviations

BTs: branched TiO2 nanotube arrays; DSSCs: dye-sensitized solar cells; FESEM: field-emission scanning electron microscopy; PCTs: P25-coated TiO2 nanotube arrays; TEM: transmission electron microscopy; TNTAs: TiO2 nanotube arrays; XRD: X-ray diffractometer.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

AH presided over and fully participated in all of the work. CC and XL participated in the preparation of the samples. JJ and RM participated in the revision of the manuscript and the statistical analysis of experimental data. JH and FW participated in the investigation of the photocurrent performances. XT and JP participated in the design and idea of the study. All authors read and approved the final manuscript.

Acknowledgements

The authors would like to acknowledge financial support for this study from the National Natural Science Foundation of China (No. 50872039; 50802032), and the Xiangyang Plans Projects of Scientific and Technological Research and Development (No. 2010GG1B35).

References

  • Iijima S. Helical microtubules of graphitic carbon. Nature. 1991;354:56. doi: 10.1038/354056a0. [Cross Ref]
  • Park S, Lim JH, Chung SW, Mirkin CA. Self-Assembly of Mesoscopic Metal-Polymer Amphiphiles. Science. 2004;303:348. doi: 10.1126/science.1093276. [PubMed] [Cross Ref]
  • Chen XB, Mao SS. Titanium Dioxide Nanomaterials: Synthesis, Properties, Modific- ations, and Applications. Chem Rev. 2007;107:2891. doi: 10.1021/cr0500535. [PubMed] [Cross Ref]
  • Zhang DF, Sun LD, Jia CJ, Yan ZG, You LP, Yan CH. Hierarchical Assembly of SnO2 Nanorod Arrays on α-Fe2O3 Nanotubes: A Case of Interfacial Lattice Compatibility. J Am Chem Soc. 2005;127:13492. doi: 10.1021/ja054771k. [PubMed] [Cross Ref]
  • Cheng CW, Liu B, Yang HY, Zhou WW, Sun L, Chen R, Yu SF, Gong H, Zhang JX, Sun HD, Fan HJ. Hierarchical Assembly of ZnO Nanostructures on SnO2 Backbone Nanowires: Low-Temperature Hydrothermal Preparation and Optical Properties. ACS Nano. 2009;3:3069. doi: 10.1021/nn900848x. [PubMed] [Cross Ref]
  • Niu MT, Huang F, Cui LF, Huang P, Yu YL, Wang YS. Hydrothermal Synthesis, Structural Characteristics, and Enhanced Photocatalysis of SnO2/α-Fe2O3 Semiconductor Nanoheterostructures. ACS Nano. 2010;4:681. doi: 10.1021/nn901119a. [PubMed] [Cross Ref]
  • Oh YS, Lee JK, Kim HS, Han SB, Park KW. TiO2 Branched Nanostructure Electrodes Synthesized by Seeding Method for Dye-Sensitized Solar Cells. Chem Mater. 2010;22:1114. doi: 10.1021/cm902272q. [Cross Ref]
  • Wang J, Lin J. Freestanding TiO2 Nanotube Arrays with Ultrahigh Aspect Ratio via Electrochemical Anodization. Chem Mater. 2008;20:1257. doi: 10.1021/cm7028917. [Cross Ref]
  • Mor GK, Shankar K, Paulose M, Varghese OK, Grimes CA. Use of Highly-Ordered TiO2 Nanotube Arrays in Dye-Sensitized Solar Cells. Nano Lett. 2006;6:215. doi: 10.1021/nl052099j. [PubMed] [Cross Ref]
  • Albu SP, Ghicov A, Aldabergenova S, Drechsel P, LeClere D, Thompson GE, Macak JM, Schmuki P. Formation of Double-Walled TiO2 Nanotubes and Robust Anatase Membranes Communication. Adv Mater. 2008;20:4135.
  • Mor GK, Shankar K, Paulose M, Varghese OK, Grimes CA. Enhanced Photocleavage of Water Using Titania Nanotube Arrays. Nano Lett. 2005;5:191. doi: 10.1021/nl048301k. [PubMed] [Cross Ref]
  • Liu L, Qian JS, Li B, Cui B, Zhou XF, Guo XF, Ding WP. Fabrication of rutile TiO2 tapered nanotubes with rectangular cross-sections via anisotropic corrosion route. Chem Commun. 2010;46:2402. doi: 10.1039/b921750a. [PubMed] [Cross Ref]
  • Yoriya S, Grimes CA. Self-Assembled TiO2 Nanotube Arrays by Anodization of Titanium in Diethylene Glycol: Approach to Extended Pore Widening. Langmuir. 2010;26:417. doi: 10.1021/la9020146. [PubMed] [Cross Ref]
  • Kim D, Ghicov A, Albu SP, Schmuki P. Bamboo-Type TiO2 Nanotubes: Improved Conversion Efficiency in Dye-Sensitized Solar Cells. J Am Chem Soc. 2008;130:16454. doi: 10.1021/ja805201v. [PubMed] [Cross Ref]
  • Kang SH, Kim JY, Kim Y, Kim HS, Sung YE. Surface Modification of Stretched TiO2 Nanotubes for Solid-State Dye-Sensitized Solar Cells. J Phys Chem C. 2007;111:9614. doi: 10.1021/jp071504n. [Cross Ref]
  • Wang DA, Liu Y, Wang CW, Zhou F, Liu WM. Highly Flexible Coaxial Nanohybrids Made from Porous TiO2 Nanotubes. ACS Nano. 2009;3:1249. doi: 10.1021/nn900154z. [PubMed] [Cross Ref]
  • Wang DA, Hu TC, Hu LT, Yu B, Xia YQ, Zhou F, Liu WM. Microstructured Arrays of TiO2 Nanotubes for Improved Photo-Electrocatalysis and Mechanical Stability. Adv Funct Mater. 2009;19:1930. doi: 10.1002/adfm.200801703. [Cross Ref]
  • Meng S, Ren J, Kaxiras E. Natural Dyes Adsorbed on TiO2 Nanowire for Photovoltaic Applications: Enhanced Light Absorption and Ultrafast Electron Injection. Nano Lett. 2008;8:3266. doi: 10.1021/nl801644d. [PubMed] [Cross Ref]
  • Paulose M, Shankar K, Varghese OK, Mor GK, Hardin B, Grimes CA. Backside illuminated dye-sensitized solar cells based on titania nanotube array electrodes. Nanotechnology. 2006;17:1446. doi: 10.1088/0957-4484/17/5/046. [Cross Ref]
  • Mohapatra SK, Misra M. Enhanced Photoelectrochemical Generation of Hydrogen from Water by 2,6-Dihydroxyantraquinone-Functionalized Titanium Dioxide Nanotubes. J Phys Chem C. 2007;111:11506. doi: 10.1021/jp0728712. [Cross Ref]
  • Mor GK, Prakasam HE, Varghese OK, Shankar K, Grimes CA. Vertically Oriented Ti-Fe-O Nanotube Array Films: Toward a Useful Material Architecture for Solar Spectrum Water Photoelectrolysis. Nano Lett. 2007;7:2356. doi: 10.1021/nl0710046. (2007) [PubMed] [Cross Ref]
  • Zheng Q, Zhou Q, Bai J, Li LH, Jin ZJ, Zhang JL, Li JH, Liu YB, Cai WM, Zhu XY. Self-Organized TiO2 Nanotube Array Sensor for the Determination of Chemical Oxygen Demand. Adv Mater. 2008;20:1044. doi: 10.1002/adma.200701619. [Cross Ref]
  • Fang XS, Bando Y, Gautam UK, Ye CH, Golberg D. Inorganic semiconductor nanostructures and their field-emission Applications. J Mater Chem. 2008;18:509. doi: 10.1039/b712874f. [Cross Ref]
  • Shin K, Seok SI, Im SH, Park JH. CdS or CdSe decorated TiO2 nanotube arrays from spray pyrolysis deposition: use in photoelectrochemical cells. Chem Commun. 2010;46:2385. doi: 10.1039/b923022j. [PubMed] [Cross Ref]
  • Macak JM, Zollfrank C, Rodriguez BJ, Tsuchiya H, Alexe M, Greil P, Schmuki P. Ordered Ferroelectric Lead Titanate Nanocellular Structure by Conversion of Anodic TiO2 Nanotubes. Adv Mater. 2009;21:3121. doi: 10.1002/adma.200900587. [Cross Ref]
  • Albu SP, Ghicov A, Macak A, Hahn R, Schmuki P. Self-Organized, Free-Standing TiO2 Nanotube Membrane for Flow-through Photocatalytic Applications. Nano Lett. 2007;7:1286. doi: 10.1021/nl070264k. [PubMed] [Cross Ref]
  • Roy P, Kim D, Lee K, Spiecker E, Schmuki P. TiO2 nanotubes and their application in dye-sensitized solar cells. Nanoscale. 2010;2:45. doi: 10.1039/b9nr00131j. [PubMed] [Cross Ref]
  • Wang J, Zhao L, Lin VSY, Lin ZQ. Formation of various TiO2 nanostructures from electrochemically anodized titanium. J Mater Chem. 2009;19:3682. doi: 10.1039/b904247d. [Cross Ref]
  • Varghese OK, Gong OK, Paulose M, Grimes CA, Dickey EC. Crystallization and high-temperature structural stability of titanium oxide nanotube arrays. J Mater Res. 2003;18:156. doi: 10.1557/JMR.2003.0022. [Cross Ref]
  • Macak JM, Gong BG, Hueppe M, Schmuki P. Filling of TiO2 Nanotubes by Self-Doping and Electrodeposition. Adv Mater. 2007;19:3027. doi: 10.1002/adma.200602549. [Cross Ref]
  • Woan K, Pyrgiotakis G, Sigmund W. Photocatalytic Carbon-Nanotube- TiO2 Composites. Adv Mater. 2009;21:2233. doi: 10.1002/adma.200802738. [Cross Ref]
  • Wang DA, Yu B, Wang CW, Zhou F, Liu WM. A Novel Protocol Towards Perfect Alignment of Defect-Free Anodized TiO2 Nanotubes. Adv Mater. 2009;21:1964. doi: 10.1002/adma.200801996. [Cross Ref]
  • Lin YJ, Zhou S, Liu XH, Sheehan S, Wang DW. TiO2/TiSi2 Heterostructures for High-Efficiency Photoelectrochemical H2O Splitting. J Am Chem Soc. 2009;131:2772. doi: 10.1021/ja808426h. [PubMed] [Cross Ref]
  • Cheng HM, Chiu WH, Lee CH, Tsai SY, Hsieh WF. Formation of Branched ZnO Nanowires from Solvothermal Method and Dye-Sensitized Solar Cells Applications. J Phys Chem C. 2008;112:16359. doi: 10.1021/jp805239k. [Cross Ref]
  • Roy P, Kim D, Paramasivam I, Schmuki P. Improved efficiency of TiO2 nanotubes in dye sensitized solar cells by decoration with TiO2 nanoparticles. Electrochem Commun. 2009;11:1001. doi: 10.1016/j.elecom.2009.02.049. [Cross Ref]
  • Prakasam HE, Shankar K, Paulose M, Varghese OK, Grimes CA. A New Benchmark for TiO2 Nanotube Array Growth by Anodization. J Phys Chem C. 2007;111:7235. doi: 10.1021/jp070273h. [Cross Ref]
  • Shankar K, Bandara J, Paulose M, Wietasch H, Varghese OK, Mor GK, LaTempa TJ, Thelakkat M, Grimes CA. Highly Efficient Solar Cells using TiO2 Nanotube Arrays Sensitized with a Donor-Antenna Dye. Nano Lett. 2008;8:1654. doi: 10.1021/nl080421v. [PubMed] [Cross Ref]
  • Xiao XF, Ouyang K, Liu RF, Liang JH. Anatase type titania nanotube arrays direct fabricated by anodization without annealing. Appl Surf Sci. 2009;255:3659. doi: 10.1016/j.apsusc.2008.10.014. [Cross Ref]
  • Pan JH, Zhang X, Du AJ, Sun DD, Leckie JO. Self-Etching Reconstruction of Hierarchically Mesoporous F-TiO2 Hollow Microspherical Photocatalyst for Concurrent Membrane Water Purifications. J Am Chem Soc. 2008;130:11256. doi: 10.1021/ja803582m. [PubMed] [Cross Ref]
  • Zuo F, Wang L, Wu T, Zhang ZY, Borchardt D, Feng PY. Self-Doped Ti3+ Enhanced Photocatalyst for Hydrogen Production under Visible Light. J Am Chem Soc. 2010;132:11856. doi: 10.1021/ja103843d. [PubMed] [Cross Ref]
  • Zhou JK, Lv L, Yu J, Li HL, Guo PZ, Sun H, Zhao XS. Synthesis of Self-Organized Polycrystalline F-doped TiO2 Hollow Microspheres and Their Photocatalytic Activity under Visible Light. J Phys Chem C. 2008;112:5316. doi: 10.1021/jp709615x. [Cross Ref]
  • Dong X, Tao J, Li YY, Zhu H. Enhanced photoelectrochemical properties of F-containing TiO2 sphere thin film induced by its novel hierarchical structure. Appl Surf Sci. 2009;255:7183. doi: 10.1016/j.apsusc.2009.03.056. [Cross Ref]
  • Park JH, Kim S, Bard AJ. Novel Carbon-Doped TiO2 Nanotube Arrays with High Aspect Ratios for Efficient Solar Water Splitting. Nano Lett. 2006;6:24. doi: 10.1021/nl051807y. [PubMed] [Cross Ref]
  • Marin FI, Hamstra MA, Vanmaekelbergh D. Greatly Enhanced Sub-Bandgap Photocurrent in Porous GaP Photoanodes. J Electrochem Soc. 1996;143:1137. doi: 10.1149/1.1836597. [Cross Ref]

Articles from Nanoscale Research Letters are provided here courtesy of Springer
PubReader format: click here to try

Formats:

Related citations in PubMed

See reviews...See all...

Cited by other articles in PMC

See all...

Links

  • PubMed
    PubMed
    PubMed citations for these articles

Recent Activity

Your browsing activity is empty.

Activity recording is turned off.

Turn recording back on

See more...